Abstract:C/C-ZrC-SiC composites were prepared by reactive melt infiltration and tested using an oxyacetylene torch with the heat fluxes of 4.18 and 2.38 MW/m(2). The results showed that compared to C/C and C/C-SiC at the heat flux of 4.18 MW/m(2), the mass ablation rates of C/C-ZrC-SiC were decreased by 60.8% and 44.8%, respectively. Its linear ablation rate was 7.3% higher than that of C/C, but was 13.5% lower than that of C/C-SiC. The C-SiC matrix and fibers of C/C-SiC in the center region were severely depleted by the high ablation temperature. C/C-ZrC-SiC composites experienced the temperature exceeding 2400 degrees C associated with intense mechanical scouring of gas flow. The severe depletion of SiC and carbon fibers on the surface led to the formation of the porous ZrO2 layer. The spallation of ZrO2 occurred in the center of the ablated surface as a result of mechanical denudation of high temperature gas flow. At the heat flux of 2.38 MW/m(2), the mass and linear ablation rates of C/C-ZrC-SiC were decreased by 76.8% and 88.4% (C/C), 66.9% and 58.3% (C/C-SiC), respectively. The oxide was slightly peeled off in the center region of C/C-SiC. The surface temperatures of C/C-SiC and C/C-ZrC-SiC were lower than that of C/C composites. The island-like ZrO2 and SiO2 layer were formed on the ablated surface of C/C-ZrC-SiC and acted as effective barriers to shield the ablation heat and slow inward transport of oxygen to the underlying material.

Ablation behavior and mechanisms of ZrC-SiC-MoSi2 coated C/C-SiC-ZrC ceramic matrix composites under oxyacetylene torch

Ablation Behavior of ZrC and ZrO2 Coatings on SiC Coated C/C Composites under Oxyacetylene Torch with Different Heat Fluxes

Ablation Behaviors and Mechanism of ZrC-SiC-Si/SiC-Si Double-Layered Coatings on C/C Composite under Plasma Flame at 3000 °C

Ablation Behavior and Mechanism of C/C–ZrC–SiC Composites under an Oxyacetylene Torch at 3000°C

Ablation performance of C/C-ZrC-SiC composites with in-situ YSi 2 -doped ZrC-SiC-ZrSi 2 coating under oxyacetylene torch

Ablation Performance of C/C-ZrC-SiC Composites with In-Situ YSi2-doped ZrC-SiC-ZrSi2 Coating under Oxyacetylene Torch

Ablation Behavior of Single and Alternate Multilayered ZrC-SiC Coatings under Oxyacetylene Torch

Ablation Resistance of Different Coating Structures for C/ZrB2–SiC Composites under Oxyacetylene Torch Flame

Effect of SiC coating on ablation resistance of C/C composites under oxyacetylene torch flame

Microstructure and Ablation Mechanism of SiC-ZrC-Al2O3 Coating for SiC Coated C/C Composites under Oxyacetylene Torch Test

Ablation Behavior of CVD-ZrC Coating under Oxyacetylene Torch Environment with Different Heat Fluxes

Ablation behaviour of the CVD-(ZrC/SiC)3 alternate coating on C/C composites under oxyacetylene torch with different heat fluxes

Ablation Behavior of C/C-ZrC-SiC Composites Prepared by Reactive Melt Infiltration under Oxyacetylene Torch at Two Heat Fluxes

Ablation Behavior of Y2SiO5/SiC Coating for C/C Composites under Oxyacetylene Torch

Preparation and ablation properties of ZrC-SiC coating for carbon/carbon composites by solid phase infiltration

Ablation Behavior of a C/C-ZrC-SiC Composite Based on High-Solid-loading Slurry Impregnation under Oxyacetylene Torch

Ablation Behavior under Oxyacetylene Torch of ZrC Coating Modified by SiC/TaC Nanocomposites

The Ablation Behavior and Mechanical Property of C/C-SiC-ZrB2 Composites Fabricated by Reactive Melt Infiltration

Ablation Behavior and Mechanism of C/C-ZrC Composites under Oxyacetylene Torch Flame

Microstructure and Ablation Performance of SiC–ZrC Coated C/C Composites Prepared by Reactive Melt Infiltration

Ablation Behavior of ZrC-SiHfOC-MoSi2 Coating for Carbon/carbon Composites under Ar-O2 Plasma Flame