Abstract:A W/ZrC/SiC multilayer coating was prepared on C/C composites by reactive melt infiltration (RMI) and atmospheric plasma spray (APS). The morphology and microstructure of the coating were characterized by scanning electron microscopy coupled with energy dispersive spectrometry (SEM‐EDS), X‐ray diffraction (XRD), focused ions beam (FIB) and transmission electron microscope (TEM). Microstructure analysis revealed that the gradient coatings exhibit smooth surface morphology, well‐defined interfaces, uniform thickness and highly dense architecture. After 60 s of ablation, the linear ablation rates (LAR) and mass ablation rates (MAR) of the coated composites stand at 2.58×10−3 mm/s and 5.25×10−3 g/s, respectively. In general, the reason for the great ablation resistance of W/ZrC/SiC coated C/C composites was the comprehensive effect of multilayer coating. The outer W coating was used as the first barrier layer to resist most thermal shocks. Then the molten eutectics SiO2‐ZrO2 formed in ZrC/SiC layer at service temperature could fill the pores and acted as a second diffusion barrier for oxygen and heat.This article is protected by copyright. All rights reserved.

Ablation behavior of ZrC-SiHfOC-MoSi 2 coating for carbon/carbon composites under Ar-O 2 plasma flame

Ablation behavior and mechanisms of ZrC-SiC-MoSi2 coated C/C-SiC-ZrC ceramic matrix composites under oxyacetylene torch

Microstructure and Ablation Performance of SiC–ZrC Coated C/C Composites Prepared by Reactive Melt Infiltration

Ablation-resistance of ZrB2-SiC Coating under Oxygen-propane Torch Flame Prepared by Atmospheric Plasma Spraying

Ablation performance of C/C-ZrC-SiC composites with in-situ YSi 2 -doped ZrC-SiC-ZrSi 2 coating under oxyacetylene torch

Ablation Resistance of APS Sprayed Mullite/ZrB2-MoSi2 Coating for Carbon/Carbon Composites

Anti-ablation performance of plasma sprayed ZrB 2 /SiC coatings on C/C substrates and the influence of a chemical vapor deposited SiC interlayer

Ablation behaviour of the CVD-(ZrC/SiC)3 alternate coating on C/C composites under oxyacetylene torch with different heat fluxes

Ablation behavior of C/C–Zr1-xHfxC-SiC composites under an oxyacetylene flame at above 2500 °C

Phase and microstructure evolutions of in-situ ZrC composite coating under plasma torch ablation

MoSi2 Addition for High Ablation Resistance of Dense ZrB2-based Composite Coating Prepared by Very Low-Pressure Plasma Spraying

Ablation behavior of ZrB2–SiC–Si composites with WC and MoSi2 additives coated through SPS on graphite

Anti-ablation Performance of Plasma Sprayed ZrB2/SiC Coatings on C/C Substrates and the Influence of a Chemical Vapor Deposited SiC Interlayer

Microstructure evolution and ablation mechanisms of Csf/ZrB2-SiC composites at different heat fluxes under air plasma flame

WSi2 modified HfB2-SiC coating: Microstructure and ablation resistance

Microstructures and ablation resistance of WSi2/ZrSi2/ZrxHf1-xC/SiC coating based on a pattern strengthening one-step method

Microstructure and Ablation Behavior of W/ZrC/SiC Coating on C/C Composites Prepared by Reactive Melt Infiltration and Atmospheric Plasma Spraying

Effect of Si, Al2O3 additives on the ablation behavior of ZrB2-SiC coating with Al2O3-modified SiC bond coat for C/C composites

Multi-cycle and long-term ablation behavior of Cf/ZrB2-SiC composites at 2500 °C

Ablation Resistance of ZrC-based Composite Coating with Multi-Layer Structure for Carbon/carbon Composites above 2200 °C

Effect of temperature-dependent nano SiC on the ablation resistance of ZrC coating