Abstract:The oxide layer formed by ultra‐high melt point oxides (ZrO2, HfO2) and SiO2 glassy melt is the key to the application of traditional thermal structural materials in extremely high‐temperature environment. However, the negative effect of ZrO2 and HfO2 phase transitions on the stability of oxide layer and rapid volatilization of low viscosity SiO2 melt limit its application in aerospace. In this study, the ablation behavior of Cf/(CrZrHfNbTa)C‒SiC high‐entropy composite was explored systematically via an air plasma ablation test, under a heat flux of 5 MW/m2 at temperatures up to 2450°C. The composite presents an outstanding ablation resistance, with linear and mass ablation rates of 0.9 μm/s and 1.82 mg/s, respectively. This impressive ablation resistance is attributed to the highly stable oxide protective layer formed in situ on the ablation surface, which comprises a solid skeleton of (Zr, Hf)6(Nb, Ta)2O17 combined with spherical particles and SiO2 glassy melt. The irregular particles provide a solid skeleton in the oxides protective layer, which increased stability of the oxide layer. Moreover, the spherical particles have a crystal structure similar to that of Ta2O5 and are uniformly distributed in SiO2 glassy melt, which hinder the flow of SiO2 glassy melt and enhance its viscosity to a certain degree. And it reduces the volatilization of SiO2. In summary, the stable oxide layer was formed by irregular particles oxide and the SiO2 glassy melt with certain viscosity, thereby resulting in the impressive ablation resistance of the composite. This study fills a gap in ablation research on the (CrZrHfNbTa)C system.

Comparison of the ablation resistance of mullite modified C/C-SiC-HfC and C/C-SiC-HfC composites under oxyacetylene flame of 2.38 MW/m 2 heat flux

Cyclic ablation behavior of mullite-modified C/C-HfC-SiC composites under an oxyacetylene flame at about 2400 °C

Ablation behavior of mullite modified C/C-SiC-HfC composites under oxyacetylene torch for single and cyclic ablations with two heat fluxes

Ablation behavior of C/C–Zr1-xHfxC-SiC composites under an oxyacetylene flame at above 2500 °C

Effect of mullite content on microstructure and ablation behavior of mullite modified C/C-SiC-HfC composites

Cyclic ablation behaviors of mullite‐modified C/C–ZrC–SiC composites prepared by PIP

Microstructure and ablation behavior of C/C–HfC–SiC composites fabricated by reactive melt infiltration with Hf–Si alloy

Long-term ablation mechanisms of the YB4-Al2O3-Si3N4 modified Cf/HfC-SiC composites at 2600 °C

Ablation behavior and mechanisms of ZrC-SiC-MoSi2 coated C/C-SiC-ZrC ceramic matrix composites under oxyacetylene torch

Effect of HfC addition on ablation behavior of SiBCN ceramics

Microstructure and Ablation Behavior of C/C-SiC-(ZrxHf1−x)C Composites Prepared by Reactive Melt Infiltration Method

Ablation behavior and mechanisms of Cf/(CrZrHfNbTa)C‒SiC high‐entropy composite at temperatures up to 2450°C

Ablation behavior and mechanisms of Cf/(Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)C–SiC high-entropy ceramic matrix composites

Microstructure and ablation resistance of C/C-HfC-SiC composites prepared by RMI with different powder particle sizes

C/C-HfC-SiC composites with simultaneous the resistance to ultra-high temperature airflow erosion and high temperature oxidation

Ablation behaviors of ultra-high temperature ceramic composites

Ablation mechanism and morphology evolution of the HfC-SiC coating for C/C composites deposited by supersonic atmospheric plasma spraying

Ablation behaviour of the CVD-(ZrC/SiC)3 alternate coating on C/C composites under oxyacetylene torch with different heat fluxes

Ablation behavior of C f /ZrC–SiC ultra–high temperature ceramic composites in oxyacetylene torch and plasma wind tunnel

Ablation performance of C/C-ZrC-SiC composites with in-situ YSi 2 -doped ZrC-SiC-ZrSi 2 coating under oxyacetylene torch

Ablation behavior and mechanisms of 3D-Cf/Ta0.8Hf0.2C-SiC composite at temperatures up to 2500 °C