Abstract:For the first time, air plasma ablation behavior of Cf/(Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)C–SiC high-entropy ceramic matrix composites was studied systematically under a heat flux of 5 MW/m2, which provided a quasi-real hypersonic service environment at a temperature up to 2430 °C. The Cf/(Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)C–SiC composites present excellent ablation-resistant performance with a linear recession rate of ∼2.89 μm/s and mass recession rate of ∼2.60 mg/s, which can be attributed to the dense and stable oxides layer formed on the sample surface. (Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)C is oxidized to high-entropy oxide (TiZrHfNbTa)Ox at the ablation center and highly viscous SiO2 melt with uniformly dispersed (TiZrHfNbTa)Ox microspheres is formed. While at the edge of the ablation center, precipitation occurs during cooling and the oxides layer turns to a plate-like (Hf0.5Zr0.5O2)’ skeleton surrounded by (TiNbTaO7-y)’ nanocrystals and continuous SiO2 melt. In contrast, oxidation of (Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)C to produce (Hf0.5Zr0.5O2)’ and (TiNbTaO7-y)’ is dominant at the ablation transition area and outer area with lower temperature. The multiphase oxides formed during ablation provide a stable and highly self-healing protective layer for the internal materials at ultra-high temperatures.

Cyclic ablation behavior of mullite-modified C/C-HfC-SiC composites under an oxyacetylene flame at about 2400 °C

Ablation behavior of mullite modified C/C-SiC-HfC composites under oxyacetylene torch for single and cyclic ablations with two heat fluxes

Comparison of the ablation resistance of mullite modified C/C-SiC-HfC and C/C-SiC-HfC composites under oxyacetylene flame of 2.38 MW/m 2 heat flux

Cyclic ablation behaviors of mullite‐modified C/C–ZrC–SiC composites prepared by PIP

Effect of mullite content on microstructure and ablation behavior of mullite modified C/C-SiC-HfC composites

Ablation behavior of C/C–Zr1-xHfxC-SiC composites under an oxyacetylene flame at above 2500 °C

Microstructure and ablation behavior of C/C–HfC–SiC composites fabricated by reactive melt infiltration with Hf–Si alloy

Cyclic ablation behavior of C/C–ZrC–SiC composites under oxyacetylene torch

Ceramic Matrix Composite Cyclic Ablation Behavior under Oxyacetylene Torch

Ablation behavior of 3D PyC-Cf/SiHfBOC Composites under an oxyacetylene torch environment above 2000 °C

Ablation Mechanism of AlSiB-C/C Composites under an Oxy-Acetylene Torch

Microstructure and Ablation Behavior of C/C-SiC-(ZrxHf1−x)C Composites Prepared by Reactive Melt Infiltration Method

Long-term ablation mechanisms of the YB4-Al2O3-Si3N4 modified Cf/HfC-SiC composites at 2600 °C

Ablation behaviors and mechanisms of Cf/HfCPIP-SiCCVI composites: From SiO2 nanowires film to HfO2 skeleton

Cyclic Ablation Properties of C/SiC-ZrC Composites

Ablation behavior and mechanisms of 3D-Cf/Ta0.8Hf0.2C-SiC composite at temperatures up to 2500 °C

Cyclic ablation behavior and microstructure evolution of multi-layer coating on C/C composites under oxyacetylene torch

Ablation behavior and mechanisms of Cf/(Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)C–SiC high-entropy ceramic matrix composites

Ablation behavior of nose-shaped HfB2-SiC modified carbon/carbon composites exposed to oxyacetylene torch

Comparative ablation behaviors of C/SiC–ZrC and C/SiC–HfC composites prepared by ceramization of carbon aerogel preforms

Oxidation/ablation behaviors of hafnium carbide-silicon carbonitride systems at 1500 and 2500 C