Abstract:The current generation of ultrahigh temperature ceramic precursors typically encounters obstacles in achieving high ceramic yields ( < 40 wt.%) due to the challenges in integrating significant amounts of boron, which hampers their conversion into boride-based ultrahigh temperature ceramics. To tackle these challenges, a serious of pioneering liquid multi-component hafnium-containing ceramic SiHfCB precursors (with different Hf/Si ratios) have been developed. These novel precursors are featured with stable molecular structure and high ceramic yield which were successfully created through a novel one-pot polymerization process. They present in liquid form and their structure is characterized by C-C bonds forming its main chain with branched chains of O-Si-O, Si-O-Hf, Si-O-B, and B-O-Hf which have untapped advantages including uniform component dispersion, and excellent fluidity. The ceramic yield of SiHfCB precursor with Hf/Si of 0.2 is remarkably up to 68.6 wt.% at 1500 degrees C, and their Hf content exceeded 50 wt.%. Of particular interest, the pyrolyzed product HfB2 -SiC nanopowders derived from the SiHfCB precursor with Hf/Si of 0.2, consist of nanopowders in the 40-60 nm range with a density of 5.23 g cm(-4). Remarkably, this material demonstrates exceptional performance in ultrahigh temperature oxygen-containing environments at 2500 degrees C, showing near-zero ablation with a linear ablation rate of just 2.5 x 10(-4) mm s(-1) . Post-ablation analysis of the microstructure reveals that the formation of a lava-like HfO2 and HfO2 -SiO2 oxide layer effectively blocks oxygen penetration and provides excellent oxidation resistance. The innovative SiHfCB hafnium-containing ceramic precursor offers a groundbreaking solution for the preparation of lightweight ultrahigh-temperature ceramics. This development is poised to provide robust technical support for the use of ultrahigh temperature ceramics in non-ablative thermal protective systems, particularly in the construction of hypersonic vehicles, where ultrahigh temperature resilience is crucial. (c) 2024 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.

Ablation behavior of 3D PyC-Cf/SiHfBOC Composites under an oxyacetylene torch environment above 2000 °C

Efficient Fabrication of Light Cf/SiHfBOC Composites with Excellent Thermal Shock Resistance and Ultra-High-temperature Ablation Up to 1800 °C

Cyclic ablation behavior of mullite-modified C/C-HfC-SiC composites under an oxyacetylene flame at about 2400 °C

Ablation behavior of mullite modified C/C-SiC-HfC composites under oxyacetylene torch for single and cyclic ablations with two heat fluxes

Ultrahigh Temperature Ablation Resistant HfB2-SiC Composites: from Liquid SiHfCB Precursor Synthesis to Light Weight Bulk Preparation and Characterization

Ablation behavior and mechanisms of 3D Cf/ZrB2-SiC composite applied in long-term temperature up to 2400 °C

Ablation behavior of nose-shaped HfB2-SiC modified carbon/carbon composites exposed to oxyacetylene torch

Ablation behavior of C/C–Zr1-xHfxC-SiC composites under an oxyacetylene flame at above 2500 °C

Ablation behavior and mechanisms of 3D-Cf/Ta0.8Hf0.2C-SiC composite at temperatures up to 2500 °C

Ablation behavior and mechanisms of Cf/(Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)C–SiC high-entropy ceramic matrix composites

Long-term ablation mechanisms of the YB4-Al2O3-Si3N4 modified Cf/HfC-SiC composites at 2600 °C

Ablation behavior and mechanisms of Cf/(CrZrHfNbTa)C‒SiC high‐entropy composite at temperatures up to 2450°C

Ablation behavior and mechanisms of 3D C<sub>f</sub>/ZrB<sub>2</sub>-SiC composite applied in long-term temperature up to 2400 C

Enhanced ablation resistance of HfB2-HfC/SiBCN ceramics under an oxyacetylene torch environment

Ablation behaviors of ultra-high temperature ceramic composites

Ablation behavior of Cf/ZrC-SiC and Cf/SiC composites produced by precursor infiltration and pyrolysis combined with gaseous silicon infiltration

Starting from essence to reveal the ablation behavior and mechanism of 3D PyC Cf/ZrC-SiC composite

Microstructure and ablation behavior of C/C–HfC–SiC composites fabricated by reactive melt infiltration with Hf–Si alloy

Effect of HfC addition on ablation behavior of SiBCN ceramics

Ablation behaviors and mechanisms of Cf/HfCPIP-SiCCVI composites: From SiO2 nanowires film to HfO2 skeleton

Cyclic ablation behavior of C/C–ZrC–SiC composites under oxyacetylene torch