Abstract:In this study, C/C–SiC and C/C–SiC–ZrC composites were prepared via chemical vapor infiltration and polymer infiltration pyrolysis, and the ablation mechanism under hypersonic oxygen-rich environmental conditions was investigated. The C/C–SiC composites demonstrate an excellent ablation resistance in a hypersonic oxygen-rich environment with a relatively low temperature and speed of approximately 1800 K and 1100 m/s, respectively. It is only in the ablation center area with higher temperatures that a certain degree of thermochemical ablation was observed. The mass and linear ablation rates of C/C–SiC composites (0.027 g/s and 0.117 mm/s, respectively) showed a significant increase in a hypersonic oxygen-rich environment with a temperature and velocity of approximately 2050 K and 2000 m/s, respectively. The high-temperature ablation resistance of ZrC-modified C/C–SiC–ZrC composites improved significantly. However, the ZrC ceramic component had a considerable impact on the ablation resistance of the material. The structural integrity of C/C–20SiC–30ZrC composites was relatively high in hypersonic oxygen-rich environments with a jet temperature and velocity of 2050 K and 2000 m/s, respectively, and mass and linear ablation rates were 0.012 g/s and 0.015 mm/s, respectively. When the ZrC content increased by 40%, the ablation resistance of the composite reduced significantly, whereas the mass and linear ablation rates increased to 0.043 g/s and 0.130 mm/s, respectively.

Starting from essence to reveal the ablation behavior and mechanism of 3D PyC Cf/ZrC-SiC composite

Ablation behavior of Cf/ZrC-SiC and Cf/SiC composites produced by precursor infiltration and pyrolysis combined with gaseous silicon infiltration

Ablation behavior and mechanisms of 3D Cf/ZrB2-SiC composite applied in long-term temperature up to 2400 °C

Microstructure and Ablation Behavior of C/C-SiC-(ZrxHf1−x)C Composites Prepared by Reactive Melt Infiltration Method

Ablation of advanced C/C-ZrC-SiC leading edge composites

Ablation behaviour of Csf/ZrB2-SiC composites fabricated by direct ink writing and reactive melt infiltration

Multi-cycle and long-term ablation behavior of Cf/ZrB2-SiC composites at 2500 °C

Ablation behavior of C f /ZrC–SiC ultra–high temperature ceramic composites in oxyacetylene torch and plasma wind tunnel

Carbon fiber reinforced ZrC based ultra-high temperature ceramic matrix composite subjected to laser ablation: Ablation resistance, microstructure and damage mechanism

Long-term ablation behavior and mechanisms of 2D-Cf/ZrB2-SiC composites at temperatures up to 2400 °C

Understanding Laser Ablating Mechanism of Cf/SiC Composites: Micro Heat Transfer and Subsurface Microstructure Transformation

Ultra-high-temperature ablation behavior of SiC–ZrC–TiC modified carbon/carbon composites fabricated via reactive melt infiltration

Study on the ablation performance of SiC-coated high thermal conductivity three-dimensional C/C composites

Microstructure evolution and ablation mechanisms of Csf/ZrB2-SiC composites at different heat fluxes under air plasma flame

Laser ablation behavior and mechanism of Cf/SiC–ZrC ultra-high temperature ceramic matrix composite prepared by PIP method

Microstructure and Ablation Performance of SiC–ZrC Coated C/C Composites Prepared by Reactive Melt Infiltration

Ablation behavior and mechanisms of Cf/(Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)C–SiC high-entropy ceramic matrix composites

Damage Mechanism Analysis to the Carbon Fiber and Fiber-Ceramic Interface Tailoring of Cf/ZrC-SiC Using PyC Coating

Oxidation behavior and ablation mechanism of Cf/ZrB2-SiC composite fabricated by vibration-assisted slurry impregnation combined with low-temperature hot pressing

Ablation mechanism of C/C–SiC and C/C–SiC–ZrC composites in hypersonic oxygen-enriched environment

Ablation performance of C/C-ZrC-SiC composites with in-situ YSi 2 -doped ZrC-SiC-ZrSi 2 coating under oxyacetylene torch