Abstract:The oxide layer formed by ultra‐high melt point oxides (ZrO2, HfO2) and SiO2 glassy melt is the key to the application of traditional thermal structural materials in extremely high‐temperature environment. However, the negative effect of ZrO2 and HfO2 phase transitions on the stability of oxide layer and rapid volatilization of low viscosity SiO2 melt limit its application in aerospace. In this study, the ablation behavior of Cf/(CrZrHfNbTa)C‒SiC high‐entropy composite was explored systematically via an air plasma ablation test, under a heat flux of 5 MW/m2 at temperatures up to 2450°C. The composite presents an outstanding ablation resistance, with linear and mass ablation rates of 0.9 μm/s and 1.82 mg/s, respectively. This impressive ablation resistance is attributed to the highly stable oxide protective layer formed in situ on the ablation surface, which comprises a solid skeleton of (Zr, Hf)6(Nb, Ta)2O17 combined with spherical particles and SiO2 glassy melt. The irregular particles provide a solid skeleton in the oxides protective layer, which increased stability of the oxide layer. Moreover, the spherical particles have a crystal structure similar to that of Ta2O5 and are uniformly distributed in SiO2 glassy melt, which hinder the flow of SiO2 glassy melt and enhance its viscosity to a certain degree. And it reduces the volatilization of SiO2. In summary, the stable oxide layer was formed by irregular particles oxide and the SiO2 glassy melt with certain viscosity, thereby resulting in the impressive ablation resistance of the composite. This study fills a gap in ablation research on the (CrZrHfNbTa)C system.

Ultra-high-temperature ablation behavior of SiC–ZrC–TiC modified carbon/carbon composites fabricated via reactive melt infiltration

Ablation behaviors of ultra-high temperature ceramic composites

Ablation behavior and mechanisms of 3D Cf/ZrB2-SiC composite applied in long-term temperature up to 2400 °C

Ablation behavior of ZrC-SiC-ZrB2 and ZrC-SiC inhibited carbon/carbon composites components under ultrahigh temperature conditions

Structural characteristics and ablative behavior of C/C–ZrC–SiC composites reinforced with “Z-pins like” Zr–Si–B–C multiphase ceramic rods

Ablation mechanism of C/C–SiC and C/C–SiC–ZrC composites in hypersonic oxygen-enriched environment

Ablation behavior and mechanisms of Cf/(CrZrHfNbTa)C‒SiC high‐entropy composite at temperatures up to 2450°C

Microstructure and Ablation Performance of SiC–ZrC Coated C/C Composites Prepared by Reactive Melt Infiltration

Ablation behavior and mechanisms of Cf/(Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)C–SiC high-entropy ceramic matrix composites

Microstructure and Ablation Behavior of C/C-SiC-(ZrxHf1−x)C Composites Prepared by Reactive Melt Infiltration Method

Effect of SiC Content on the Ablation and Oxidation Behavior of ZrB2-Based Ultra High Temperature Ceramic Composites

Progress in preparation and ablation resistance of ultra-high-temperature ceramics modified C/C composites for extreme environment

Intelligent cooling structure design of "Z-pins like" silicon rods to enhance the ablation resistance of C/C-ZrC-SiC composites above 2500 °C

Ablation behavior of C f /ZrC–SiC ultra–high temperature ceramic composites in oxyacetylene torch and plasma wind tunnel

Oxidation behavior and ablation mechanism of Cf/ZrB2-SiC composite fabricated by vibration-assisted slurry impregnation combined with low-temperature hot pressing

Ablation behavior of C/C–Zr1-xHfxC-SiC composites under an oxyacetylene flame at above 2500 °C

Ablation behavior and mechanisms of 3D-Cf/Ta0.8Hf0.2C-SiC composite at temperatures up to 2500 °C

Microstructure and ablation behaviour of C/C-SiC-ZrC-Cu composites prepared by reactive melt infiltration

Preparation and flame ablation/oxidation behavior of ZrB2/SiC ultra-high temperature ceramic composites

Long-term ablation behavior and mechanisms of 2D-Cf/ZrB2-SiC composites at temperatures up to 2400 °C

Study on the ablation performance of SiC-coated high thermal conductivity three-dimensional C/C composites