Abstract:In order to improve the ablation and oxidation resistance of C/C–ZrC–SiC composites in wide temperature domain, "Z-pins like" Zr–Si–B–C multiphase ceramic rods are prepared in the matrix. The influence of different sintering temperatures on the microstructure of ceramic rods and the ablative behavior of heterogeneous composites are studied. The results showed that the ZrB2 and SiC phases are formed in the sintered matrix, and the increase of sintering temperature is beneficial to improve the density of the ceramic rods. The ablation properties of samples have been greatly improved. The mass and linear ablation rate are 0.8 mg/s and 3.85 μm/s, respectively, at an ablation temperature of 3000 °C and an ablation time of 60 s. After ablation, the matrix surface is covered with SiO2 and ZrO2 mixed oxide films. This is due to the preferential oxidation of "Z-pins like" Zr–Si–B–C multiphase ceramic rods in the ablation process, and B2O3 melt, SiO2 melt, borosilicate glass, ZrSiO4 melt and ZrO2 oxide film can be generated successively from the low-temperature segment to the ultra-high temperature segment. These oxidation products can be used as compensation oxide melts for the healing of cracks and holes on the matrix surface in different temperature ranges and effectively prevent the external heat from spreading into the matrix. Therefore, C/C–ZrC–SiC composites with "Z-pins like" Zr–Si–B–C multiphase ceramic rods achieve ablation resistance in wide temperature domain.

Intelligent cooling structure design of "Z-pins like" silicon rods to enhance the ablation resistance of C/C-ZrC-SiC composites above 2500 °C

Structural characteristics and ablative behavior of C/C–ZrC–SiC composites reinforced with “Z-pins like” Zr–Si–B–C multiphase ceramic rods

Ablation Behaviors and Mechanism of ZrC-SiC-Si/SiC-Si Double-Layered Coatings on C/C Composite under Plasma Flame at 3000 °C

Optimization of 3D Inlay Mode of “Z-Pins Like” V0.9-Si0.1 Rods and Their Improvement Effect on the Anti-Ablative Performance of C/C-ZrC-SiC

A novel optimized two-step method for preparing the Z-pin-like rods to improve their effect on the ablation resistance of C/C-ZrC-SiC

Novel “Z-Pins Like” Vanadium Rods Prepared by Solid Phase Sintering to Improve Ablation Resistance of the C/C-ZrC-SiC Composites

Novel one-step formed composite reinforcement of "Spider web like" SiCnw networks and "Z-pins like" SiC rods for ablation resistance improvement of C/C-ZrC-SiC

Effect of surface structure unit of 3D needled carbon fiber preform on the ablation improvement of “Z-pins like” V0.9-Si0.1 rod for C/C–ZrC–SiC

Microstructure and High Temperature Anti-Ablation Behavior of Cr-modified ZrC Coating for SiC-coated Carbon/carbon Composites

Enhanced Anti-Ablation Performance of Carbon/carbon Composites Modified with ZrC-SiC

Ultra-high-temperature ablation behavior of SiC–ZrC–TiC modified carbon/carbon composites fabricated via reactive melt infiltration

Ablation Behavior of Zr–Al(Si)–C Layered Carbides Modified 3D Needled C/SiC Composites

The Ablation Behavior and Mechanical Property of C/C-SiC-ZrB2 Composites Fabricated by Reactive Melt Infiltration

Ablation Performances of Multi-Phased C/C-Zrc-Sic Ultra-High Temperature Composites

Multi-cycle and long-term ablation behavior of Cf/ZrB2-SiC composites at 2500 °C

Ablation Mechanism and Properties of SiO2 Modified ZrB2-SiC Coatings Fabricated on C/C Composites Via Plasma Spraying Technology

Ablation behavior and mechanisms of 3D C<sub>f</sub>/ZrB<sub>2</sub>-SiC composite applied in long-term temperature up to 2400 C

Long-life ablation resistance ZrB<sub>2</sub>-SiC-TiSi<sub>2</sub> ceramic coating for SiC coated C/C composites under oxidizing environments up to 2200 K

Ablation Behavior and Mechanism of C/C–ZrC–SiC Composites under an Oxyacetylene Torch at 3000°C

Microstructure, Mechanical and Ablation Properties of Transpiration Cooling Applied to C/C-SiC Composite for Novel Anti-ablation Material

Oxidation behavior and ablation mechanism of Cf/ZrB2-SiC composite fabricated by vibration-assisted slurry impregnation combined with low-temperature hot pressing