Abstract:Objectives To investigate transient thermal stresses that developed in 3Y-TZP green compacts during speed sintering. Methods A total of 312 disc-shaped green compacts (Ø17.1 ×1, 1.5, 2, 2.5, 3 mm) were cold-isostatically pressed from 3Y-TZP powder (Zpex, Tosoh Corp.) for speed sintering studies as well as compositional analysis and biaxial flexural strength measurements (both at room temperature and following heating at 90 °C/min to 500 °C). Flexural strength was determined using the piston-on-3-ball method. Phase assemblies were analyzed using the X-ray diffraction method. Effects of heating/cooling rates on transient stresses were investigated by conducting definitive sintering studies to determine the threshold for fracture. Finite element analysis (FEA) was used to validate the experimental findings using measured thermomechanical properties. Results The bulk and relative density of the green compact were 2.95 ± 0.03 g/cm 3 and 48.52% ± 0.45%. The flexural strength was drastically decreased from 10.3 ± 0.4 MPa to 1.09 ± 0.07 MPa following heating at 90 °C/min to 500 °C. The monoclinic and tetragonal contents were 54.9% and 45.1%, respectively. The threshold for fracture was located at 500 °C during the first heating stage with a 90 °C/min heating rate in specimens of 2.5 mm thickness or greater. No fractures occurred in the second heating stage and cooling phase. The FEA estimated that the principal transient tensile stress was ∼1.14 MPa at 500 °C during the heating phase, which exceeded the corresponding flexural strength (1.09 ± 0.07 MPa). Significance Advanced FEA methods are an accurate and efficient tool to analyze the history of transient stresses during sintering of ceramic dental restorations.

R-Curve Determination of 3Y-Psz by the Indentation Strength-In-Bending Method

Characterization of R-curve Behavior in Si3N4-based Ceramics

Residual stress distributions around indentations and crack in 3Y-TZP ceramics measured using piezo spectroscopy

R-curve Behavior of Indentation Cracks in Silicon Nitride Based Ceramic Composite

R‐Curve Behavior of 3Y‐TZP at Cryogenic Temperatures

Slow Crack Growth Behavior of 3Y-TZP in Cryogenic Environment Using Dynamic Fatigue and Indentation Technique

Spherical Indentation and Implementation of S 3 /P for Yield Stress Determination of Brittle Materials

Crack-Location-Dependent R-Curve Behavior in Si3n4

Determination of cyclic R-curve for predicting short fatigue crack growth

Subcritical crack growth behavior and life data analysis of two types of dental Y-TZP ceramics

Transformation Driving Force for Indentation Cracking in Zirconia Ceramics

High Temperature Indentation Tests of YSZ Coatings in Air Up to 1200 °C

Micromechanical characterization of zirconia and silicon nitride ceramics using indentation and scratch methods

Transient thermal stresses developed during speed sintering of 3 mol% yttria-stabilized tetragonal zirconia polycrystals

Assessing fracture toughness in sintered Al2O3–ZrO2(3Y)–SiC ceramic composites through indentation technique

IMPROVEMENT ON THE ENVELOPE METHOD EVALUATING R-CURVE OF CERAMICS

Cyclic fatigue resistance of yttria-stabilized tetragonal zirconia polycrystals with hot isostatic press processing

Strength/Crack-Size Relationship for Knoop-Indented Bending Specimens and Its Application to Silicon Nitride Ceramics

R-curve of La2O3 doped Zirconia Toughened Alumina Composites Prepared via Stereolithography based 3D Printing

On the feasibility of the Chevron Notch Beam method to measure fracture toughness of fine-grained zirconia ceramics

Herzian Contact Fatigue Test of Y-PSZ and Y-PSZ/Al2O3 Ceramics in Hot Water.