Abstract:A one-step route was developed to fabricate Cu(In,Ga)Se2 (CIGS) absorber layers by direct magnetron sputtering from a single quaternary target with the composition of CuIn0.75Ga0.25Se2. The effects of the substrate temperature, the working pressure and the sputtering power on the morphology and phase structure of the CIGS layers were studied using scanning electron microscopy, X-ray diffraction and Raman spectroscopy. The microstructure properties of the layers, including the crystallinity, grain size, compactness and the surface evenness, were found to be strongly dependent on the deposition parameters. CIGS absorbers with compact microstructure and large grains of micrometer size were obtained at 400°C and 160W, showing a very strong (220)/(204) orientation preference when sputtered at a higher working pressure. Raman spectra indicated no precipitation of the Cu–Se binary phases, but revealed a slight difference in the Ga/(Ga+In) ratio of different layers. The overall composition of the as-sputtered CIGS film was confirmed to be in agreement with the target composition through energy dispersive X-ray spectroscopy study. In comparison with the conventional co-evaporation or post-selenization synthesis for CIGS, the one-step sputtering route is more simplified and economical, which shows great potential to reduce the production cost of CIGS-based solar cells.

Fabrication of Se-rich Cu(In1-XGaX)Se2 Quaternary Ceramic Target

Preparation and performances of high density Cu(In, Ga)Se3 ceramic targets

The Formation Mechanism of Cu(In0.7Ga0.3)Se-2 Nanoparticles and the Densification Trajectory of the Se-Rich Quaternary Target by Hot Pressing

Fabrication of Cu(In, Ga)Se-2 Thin Films by Sputtering from A Single Quaternary Chalcogenide Target

Preparation of Cu(In,Ga)Se2 Thin Film by Sputtering from Cu(In,Ga)Se2 Quaternary Target

The Effects of Selenium Content on Cu(Inga)Se-2 Thin Film Solar Cells by Sputtering from Quaternary Target with Se-Free Post Annealing

The Relationships Between Electronic Properties and Microstructure of Cu(In,Ga)Se-2 Films Prepared by Sputtering from A Quaternary Target

Influences of Ga Concentration on Performances of CuInGaSe2 Cells Fabricated by Sputtering-Based Method with Ceramic Quaternary Target

Fabricating Cu(In,Ga)Se2 (CIGS) Thin Films with Large Grains Based on the Quaternary CIGS Targets

Influences of Na on Sintering of Cu(In, Ga)Se-2 Quaternary Ceramic Targets

10.3%-Efficient Submicron-Thick Cu(In,Ga)Se2 Solar Cells with Absorber Fabricated by Sputtering In2Se3, CuGaSe2 and Cu2Se Targets

Synthesis and Characterization of CIGS Powder

Structure and Conductivity of Cu(In0.7Ga0.3)Se-2 Target Processed by Spark Plasma Sintering

One-Step Synthesis of Cu(In,Ga)Se-2 Absorber Layers by Magnetron Sputtering from A Single Quaternary Target

Fabrication of Cu(In,Ga)Se2 thin films solar cell by selenization process with Se vapor

Cu(In,Ga)Se-2 Solar Cells Fabricated by Sputtering from Copper-Poor and Selenium-Rich Ceramic Target with Selenium-Free Post Treatment

Cu(In,Ga)Se2 solar cell with 16.7% active‐area efficiency achieved by sputtering from a quaternary target

Research progress on synthesis of CuIn1-x Gax Se2 nanoparticles

Influence of Se Supply for Selenization of Cu(In,Ga)Se-2 Precursors Deposited by Sputtering from A Single Quaternary Target

Fabrication of Cu(In,Ga)Se-2 Thin Films from Nanoparticles by Non-Vacuum Mechanochemical Method and Rapid Thermal Annealing Process

Research progress on synthesis of CuIn 1-xGa xSe 2 nanoparticles