Design, Fabrication and Dielectric Properties in Core–double Shell BaTiO3-based Ceramics for MLCC Application

Hua Hao,Mengying Liu,Hanxing Liu,Shujun Zhang,Xin Shu,Ting Wang,Zhonghua Yao,Minghe Cao

DOI: https://doi.org/10.1039/c4ra13367f

IF: 4.036

2015-01-01

RSC Advances

Abstract:BaTiO3-based ceramics with a core–double shell structure were fabricated by precipitation and the sol–gel method.

What problem does this paper attempt to address?

Modeling of the Core-Shell Microstructure of Temperature-Stable Batio3 Based Dielectrics for Multilayer Ceramic Capacitors

Hai Wen,Xiaohui Wang,Zhilun Gui,Longtu Li

DOI: https://doi.org/10.1007/s10832-007-9240-1

2007-01-01

Journal of Electroceramics

Abstract:A simplified model was proposed for the core-shell microstructure, which existed in the temperature-stable BaTiO3 (BT) based dielectrics for multilayer ceramic capacitors (MLCCs) and was regarded as the reason resulting in the temperature-stable characteristics. In this model the capacitance of a core-shell grain can be regarded as the parallel combination of the capacitance of the grain core and the grain shell. To verify the validity of the model, core material, shell material and core-shell material were prepared. Based on our previous work, BT with a grain size of 400 nm was chosen as the core material; X7R material milled for 1 hour was chosen as the core-shell material; doped BT milled for 36 h was chosen as the shell material. The calculated results showed good agreement with the measured experimental results of the core-shell material, which proved the validity of the model.
Formation of Core‐Shell Structure in Ultrafine‐Grained BaTiO3‐Based Ceramics Through Nanodopant Method

Zhibin Tian,Xiaohui Wang,Yichi Zhang,Jian Fang,Tae-Ho Song,Kang Heon Hur,Seungju Lee,Longtu Li

DOI: https://doi.org/10.1111/j.1551-2916.2009.03371.x

IF: 4.186

2010-01-01

Journal of the American Ceramic Society

Abstract:The formation of core‐shell structure is the key issue of temperature stable barium titanate‐based dielectric ceramic for multilayer ceramic capacitor application. It is difficult to obtain and observe the core‐shell structure in ceramic grains when the grain size becomes smaller, especially to sizes <200 nm. A nanodopant method has been developed for the preparation of ultrafine‐grained barium titanate‐based ceramics with grain size below 200 nm. The existence of core‐shell structure was proved by transmission electron microscopy observation and energy‐dispersive spectroscopy analysis. High‐performance X7R dielectric ceramics were produced in a reducing atmosphere by normal sintering and two‐step sintering method. The dielectric constant at room temperature could reach over 2000, with a low dielectric loss at about 1.0% and high insulation resistivity ∼1012Ω·cm.
Core-shell structure in nanocrystalline modified BaTiO3 dielectric ceramics prepared by different sintering methods

Zhibin Tian,Xiaohui Wang,Huiling Gong,TaeHo Song,KangHeon Hur,Longtu Li

DOI: https://doi.org/10.1111/j.1551-2916.2010.04357.x

IF: 4.186

2011-01-01

Journal of the American Ceramic Society

Abstract:The modified BaTiO3 dielectric ceramics have been prepared by different sintering methods with grain size of similar to 100 nm. The dielectric properties, core-shell structure, and the dopant distribution in ceramic grains were studied. It is found that the diffuse phase transition peak shifts to the lower temperature as the sintering process changes from conventional sintering to two-step sintering, which improves the temperature coefficient of capacitance performance at the low-temperature end. The results are beneficial to develop the ultra-thin active layer (< 1 mu m) multilayer ceramic capacitors and better control of the well-defined core-shell structures in nano-BaTiO3 grains to maintain the temperature stability.
Dielectric Performance and Conductive Mechanism of KNN-based Ceramics Prepared Via Sol–gel Core–shell Process

Zhou Yu,Fang Bijun,Zhang Shuai,Lu Xiaolong,Ding Jianning

DOI: https://doi.org/10.1007/s10854-022-08077-0

2022-01-01

Journal of Materials Science Materials in Electronics

Abstract:0.95(Li0.02Na0.50K0.48)(Nb0.95Sb0.05)O3–0.05AgTaO3@BaZrO3 (LNKNbSAT@BZ) lead-free ceramics were prepared via a sol–gel core–shell process, in which the LNKNbSAT core particles with 150–200 nm were prepared by solid-phase method and the “BaZrO3” shell with 5–6 nm was prepared by sol–gel technique. The sol–gel core–shell process synthesized LNKNbSAT@BZ powders exist in submicron and present uniform distribution of elements, which improves reaction activity and reduces calcination temperature. The LNKNbSAT@BZ ceramics calcined at 775 °C and sintered at 1150 °C exhibit pure perovskite phase, large density, and excellent electrical properties, correlating with the coexistence of rhombohedral and tetragonal phases and the sol–gel core–shell process utilized in this work. The LNKNbSAT@BZ ceramics approach to normal ferroelectrics with partially diffused phase transition characteristics proved by the Curie–Weiss law and the exponential law fitting simultaneously. The LNKNbSAT@BZ ceramics show thermal activation relaxation behavior, and the high-temperature Cole–Cole impedance performance can be fitted well by the two equivalent circuits (RQC) connected in series. Such space charges effect conforms to the Arrhenius relationship, which presents a hopping-type process and relates to oxygen vacancies produced by the evaporation of alkali metals during sintering.
Effects of Processing on Microstructure and Dielectric Properties of Ultrafine- Grained Barium Titanate Based Ceramics for BME-MLCC Applications

Tian Wang,Xiaohui Wang,Guofeng Yao,Yichi Zhang,Xunxun Liao,Gang Yang,Tae-Ho Song,Longtu Li

DOI: https://doi.org/10.4028/www.scientific.net/kem.368-372.43

2008-01-01

Key Engineering Materials

Abstract:Ultrafine-grained ceramics based on nano-scale barium titanate for BME-MLCC applications have been prepared. Relationships of milling time, microstructures and dielectric properties have been investigated. With processing selected carefully, the present ceramics show ultrafine grain size (180nm) and homogeneous microstructures, well with high dielectric constant (ε25=2550), low dielectric loss (<0.02), high resistivity, high breakdown field and X7R temperature specifications, which would be promising materials for the next generation BME-MLCC applications.
High DC-Bias Stability and Reliability in BaTiO3-Based Multilayer Ceramic Capacitors: the Role of the Core-Shell Structure and the Electrode

Weichen Zhang,Ying Jiang,Mengjian Xiao,Yichao Zhen,Chaoqiong Zhu,Peiyao Zhao,Kezhen Hui,Limin Guo,Xu Cheng,Zhenxiao Fu,Xiuhua Cao,Xiaohui Wang

DOI: https://doi.org/10.1021/acsami.3c16740

IF: 9.5

2023-01-01

ACS Applied Materials & Interfaces

Abstract:With the miniaturization of multilayer ceramic capacitors (MLCCs) and the increase of the electric field on a single dielectric layer, dielectric constant DC-bias stability and reliability have gradually aroused attention in the advanced electronics industry. In this study, MLCCs with outstanding DC-bias stability and reliability were prepared by using dielectric ceramic optimization and electrode optimization strategies. The effect of the Dy-Y doping concentration on the microstructure, dielectric properties, and reliability of BaTiO3-based ceramics was investigated. The shell ratio and effective shell doping concentration of the core-shell structure in ceramic grains play important roles in defects and electrical performances. The ceramic with appropriate doping contents shows a dielectric constant of 1800 and a dielectric constant change rate of -17% under a DC field of 4 kV/mm, which was fabricated into prototype MLCCs with different Ni electrodes. MLCCs exhibit outstanding DC-bias stability with a -28% degradation in the dielectric constant under a DC field of 4 kV/mm while possessing a dielectric constant of 2300 and satisfying the EIA X7S specification. Additionally, it was discovered that MLCCs prepared by using fine-size Ni particle electrodes have low electrode roughness and high interfacial Schottky barriers, resulting in better reliability. This study provides promising candidate materials and theoretical references for high-end and high DC-bias stability MLCCs.
Microstructures and Dielectric Characteristics of Ultrafine-Grained Barium Titanate-Based Ceramics for Base-Metal-Electrode Multilayer Ceramic Capacitors Applications

Tian Wang,Xiaohui Wang,Tae-Ho Song,Longtu Li

DOI: https://doi.org/10.1143/jjap.46.6751

IF: 1.5

2007-01-01

Japanese Journal of Applied Physics

Abstract:Ultrafine-grained ceramics based on barium titanate for base-metal-electrode multilayer ceramic capacitors (BME-MLCCs) applications have been prepared. X-ray diffraction analysis was used to identify the phase compositions of the ceramics. The microstructures were characterized by scanning electron microscopy and transmission electron microscopy. The effects of different dopant contents on the crystal structures, grain growth, microstructures, and dielectric characteristics of the ceramics were investigated. Desired core–shell structures have been observed and the relationships of composition, crystal structure, grain growth, and microstructure have been discussed. The present ceramics show an average grain size of 180 nm and homogeneous microstructures, as well as a high dielectric constant, a low degree of dielectric loss and good X7R temperature characteristics, which would be promising candidates for next-generation BME-MLCC applications.
Influence of Sintering Temperature on Core–shell Structure Evolution and Reliability in Dy Modified BaTiO3 Dielectric Ceramics

Huiling Gong,Xiaohui Wang,Shaopeng Zhang,Xinye Yang,Longtu Li

DOI: https://doi.org/10.1002/pssa.201400013

2014-01-01

Abstract:The formation of core–shell structure plays a very important role in temperature stable BaTiO3‐based dielectric ceramic for multilayer ceramic capacitors applications. In this work, the rare earth Dy modified BaTiO3 dielectric ceramics have been prepared by chemical coating method, which possess high dielectric constant and high insulation resistivity, satisfying the EIA X7R specification. The existence of core–shell structure was proven by transmission electron microscopy observation and energy dispersive spectroscopy analysis. Experimental results show that the sintering temperature has a strong effect on the core–shell structure evolution in Dy‐doped BaTiO3 ceramics. Thus, selecting an appropriate sintering temperature is conducive for improving the temperature stability for multilayer ceramic capacitors applications. Furthermore, impedance analysis and the highly accelerated lifetime test show that the core–shell structure evolution has a closely relationship with the reliability accompanied by the increasing of sintering temperatures.
Exceptional Dielectric Performance of MLCCs Enabled by Defect-Engineered BaTiO3

Pengfei Wang,Xiong Huang,Saiwei Luan,Jianwei Zhao,Bo Li,Jun Yang,Zhenxiao Fu,Xiuhua Cao,Lei Zhang,Shuhui Yu,Rong Sun

DOI: https://doi.org/10.1039/d4tc01762e

IF: 6.4

2024-01-01

Journal of Materials Chemistry C

Abstract:It is deficient to achieve an in-depth understanding of Ba/Ti ratio on performance from the perspective of defect chemistry in BaTiO3 (BT) based multilayer ceramic capacitors (MLCC) due to the...
Boosting Effective Capacitance of Nano-Grained Batio3-Based Ceramics Via a Precise Core-Shell Structure Optimization Strategy

Chaoqiong Zhu,Ziming Cai,Mengjian Xiao,Ying Jiang,Peizhong Feng,Shiheng Li,Xiuhua Cao,Zhenxiao Fu,Xiaohui Wang

DOI: https://doi.org/10.1016/j.jallcom.2024.174037

IF: 6.2

2024-01-01

Journal of Alloys and Compounds

Abstract:The continued miniaturization of multilayer ceramic capacitors (MLCCs) means that thinner dielectric layers are exposed to stronger electric fields, degrading their capacitance. Thus, improving the DC-bias stability is urgent to maintain capacitance under strong electric fields and satisfy the requirements of high-end MLCCs. This work proposes a strategy for optimizing the DC-bias performance by tuning the core-shell structure of ceramics. Both numerical and experimental results indicate that the DC-bias performance of core-shell-structure ceramics can be significantly optimized under the double action of thickening the shell and increasing the shell dielectric constant, which simultaneously achieves considerable dielectric constant under DC-bias. Dy-Mg co-doped BaTiO 3 - based ceramics with an average grain size of about 180 nm prove extremely DC-bias stability and have a high dielectric constant of about 2000 and a low DC-bias attenuation coefficient of -23.6% at 4 kV/mm, which guarantees a high effective capacitance, especially under high electric fields.
High DC-Bias Stability and Reliability in BaTiO 3 -Based Multilayer Ceramic Capacitors: The Role of the Core-Shell Structure and the Electrode

Weichen Zhang,Ying Jiang,Mengjian Xiao,Yichao Zhen,Chaoqiong Zhu,Peiyao Zhao,Kezhen Hui,Limin Guo,Xu Cheng,Zhenxiao Fu,Xiuhua Cao,Xiaohui Wang

DOI: https://doi.org/10.1021/acsami.3c16740

IF: 9.5

2023-12-26

ACS Applied Materials & Interfaces

Abstract:With the miniaturization of multilayer ceramic capacitors (MLCCs) and the increase of the electric field on a single dielectric layer, dielectric constant DC-bias stability and reliability have gradually aroused attention in the advanced electronics industry. In this study, MLCCs with outstanding DC-bias stability and reliability were prepared by using dielectric ceramic optimization and electrode optimization strategies. The effect of the Dy-Y doping concentration on the microstructure,...

materials science, multidisciplinary,nanoscience & nanotechnology
Medium Temperature Sintered BaTiO3-based Ceramics for X8R Capacitors

Xinyue Zhang,Junlei Qi,Yiqian Liu,Jinghan Cai,Yuan-hua Lin

DOI: https://doi.org/10.1016/j.jmat.2024.02.005

IF: 8.589

2025-01-01

Journal of Materiomics

Abstract:The development of X8R BaTiO3-based dielectric materials is of great significance for the high-temperature application of MLCCs. Herein, a series of BaTiO3-based dielectric ceramics were prepared by the conventional solid-state method, and the effects of Bi4Ti3O12 and Mn3O4 on the properties of BaTiO3-based dielectric ceramics were studied. The SEM images show that the addition of Bi4Ti3O12 with a low melting point can densify the ceramics at a lower sintering temperature (1,150 degrees C). TEM images and EDS results indicate that the samples have a "core-shell" structure, which can be optimized by Bi4Ti3O12, resulting in phase transition dispersion and thus improving the temperature stability of the material. The addition of Mn can reduce the dielectric loss of ceramics at high temperatures. As a result, the optimal composition exhibits a high permittivity of 2,090, a low dielectric loss of 1.1%, and high temperature stability satisfying the X8R specification. (c) 2024 The Authors. Published by Elsevier B.V. on behalf of The Chinese Ceramic Society.
Defect Control of Yb-doped Dielectric Ceramics on Improving the Reliability for MLCC Application

Yichao Zhen,Mengjian Xiao,Xu Cheng,Chaoqiong Zhu,Yan Yu,Xiaohui Wang

DOI: https://doi.org/10.1016/j.ceramint.2022.12.061

IF: 5.532

2023-01-01

Ceramics International

Abstract:A fine-grained Yb-doped (Ba1-xCax)mTiO3 (BCT)-based ceramic, possessing high dielectric properties and outstanding reliability under a reducing atmosphere sintering, was synthesized by the chemical coating method. The mean grain size of the ceramics was 170 nm. A distinct core-shell structure of ceramics was observed by the TEM-EDS measurement. With increasing content of Yb, the curie temperature increased and the DC-bias capacitance change rate decreased under a DC field at 40 kV/cm. The optimal component showed a dielectric constant of 2200 and met the requirement of the X8R MLCCs application. Moreover, the outstanding highly accelerated life-time and higher grain boundary activation energy substantiated that Yb dopant prominently improved the reliability of dielectric materials of MLCCs. All these studies provide meaningful recommendations for the research on dielectric materials of high-performance, high-reliability base-metal MLCCs.
Preparation of Nano BaTiO3-Based Dielectric Ceramics by Different Sintering Methods

Huiling Gong,Xiaohui Wang,Jinyong Kim,Zhibin Tian,Guofeng Yao,Longtu Li

DOI: https://doi.org/10.4028/www.scientific.net/kem.512-515.1136

2012-01-01

Key Engineering Materials

Abstract:Microstructure control in thin-layer multilayer ceramic capacitors (MLCCs) is one of the nowaday challenges for increasing capacitive volumetric efficiency and high voltage dielectric properties. In this paper, the ultrafine-grained BaTiO3 dielectric ceramics with uniform grain size distribution were prepared by chemical coating approach. The doping effects of rare-earth element (Ho) on the microstructures and dielectric properties of the ceramics were investigated. The addition of Ho in nano BaTiO3-based ceramics was found to improve the temperature coefficient of capacitance (TCC) performance, which could be attributed to a significant reduction in the grain size. Moreover, the effects of two-step sintering (TSS) method on the microstructures and dielectric properties, compared with conventional sintering (CS) method, were also discussed. The dielectric constant of ceramics sintered by the TSS method was higher than that of ceramics prepared by CS method. The results reveal that the adoption of TSS method could control the grain size and suppress the abnormal grain growth more effectively, which improves the TCC characteristics.
Diffusion and Defect Chemistry of Temperature-Stable BaTiO3-based Ceramics: Experiment and Theoretical Calculations

Xu Cheng,Yichao Zhen,Mengjian Xiao,Peiyao Zhao,Kezhen Hui,Weichen Zhang,Ying Jiang,Limin Guo,Zhenxiao Fu,Xiuhua Cao,Hong Wang,Xiaohui Wang

DOI: https://doi.org/10.1016/j.jeurceramsoc.2024.116825

IF: 5.7

2025-01-01

Journal of the European Ceramic Society

Abstract:The ion diffusion and defect chemistry are the key factors in constructing the core-shell structure and improving the dielectric properties in temperature-stable BaTiO3-based dielectric ceramics. In this work, the BaTiO3-based ceramics doped with various rare-earth (RE) elements are prepared via the chemical coating method. The metal vacancy assisted A-B jumping migration path is confirmed as the main migration mechanism, where larger RE ions migrate faster and facilitate grain growth. About ~1mol % of amphoteric rare-earth ions are necessary to trap the oxygen vacancies and increase the activation energy and depolarized temperature. The electron paramagnetic resonance and thermodynamic model reveals that Mn4+ is not detected in all samples and the content of Mn2+ is determined by the Fermi level of the systems, influenced by the donor/acceptor doping, concentrations, and oxygen partial pressure. This work provides support for the rational design of dielectric materials with excellent dielectric performance and good reliability.
Nb-doped BaTiO3-(Bi0.5Na0.5)TiO3ceramics with Core-Shell Structure for High-Temperature Dielectric Applications

Z. B. Shen,X. H. Wang,D. S. Song,L. T. Li

DOI: https://doi.org/10.1080/17436753.2016.1181814

2016-01-01

Advances in Applied Ceramics

Abstract:Nb-doped 0.90BaTiO(3)-0.10(Bi0.5Na0.5)TiO3 temperature-insensitive ceramics with novel core-shell structure were sintered at low temperature by the conventional solid-state reaction method. The beneficial role of Nb in facilitating the formation of core-shell structure because of chemical inhomogeneity is verified, which is responsible for the weak temperature dependence of dielectric properties. Temperature dependence of permittivity measured at different frequencies shows high frequency dispersion at low temperature, while without relaxor characteristic at high temperature. The Vogel-Fulcher model was adopted to study the relaxor behaviour of Nb-doped 0.90BaTiO(3)-0.10(Bi0.5Na0.5)TiO3 ceramics at low temperature. The samples with an addition of 1.5 mol% Nb2O5 provide a temperature coefficient of capacitance meeting the requirements of the X9R characteristic, and result exhibits an optimum dielectric behaviour of epsilon(r) similar to 1900, tan delta similar to 1.8% at room temperature, making the material a promising candidate for high temperature applications.
Fabrication of BaTiO 3 nanopowders with high tetragonality via two-step assisted rotary furnace calcination for MLCC applications

Saiwei Luan,Shaokang Si,Lei Zhang,Pengfei Wang,Gang Jian,Jun Yang,Shuhui Yu,Rong Sun,Zhenxiao Fu,Xiuhua Cao

DOI: https://doi.org/10.1016/j.ceramint.2022.12.113

IF: 5.532

2023-03-08

Ceramics International

Abstract:Ultrafine ceramic powders with high tetragonality are essential for next-generation multi-layer ceramic capacitors (MLCC). The solid-state reaction synthesis commonly used in industry is challenging to prepare ultra-fine BaTiO 3 powders due to issues of the coarse crystallization at high temperature calcinations. In this study, a two-step calcination combining with the rotary furnace was innovatively used to synthesize ultra-fine BaTiO 3 powders with uniform particle and high tetragonality. Through the reaction kinetics study, it was found that the rotary furnace increases the point contact area of Ba 2+ and Ti 4+ by improving the heat transfer efficiency of the solid-phase reaction and decreases the diffusion rate of both, so that the diffusion-nucleation-growth rate is greater than the decomposition rate of BaCO 3 to improve the tetragonality of BaTiO 3 powders. The optimal process parameters were determined and the reaction mechanism was studied. Particularly, the optimized two-step assisted rotary furnace calcination had succeeded in preparing finer powders with an average particle size of 250 nm and tetragonality ( c / a ) of 1.0096. The BaTiO 3 ultrafine powders sintered at 1200 °C has a ceramic density of 96%, dielectric constant of 9173 at the Curie temperature point (131 °C) and a grain activation energy of 0.821 eV, representing excellent dielectric properties and reliability.

materials science, ceramics
Ultrafine grained BaTiO3 based ceramic material for temperature stable BME MLCCs

XH Wang,H Zhou,H Wen,RZ Chen,X Li,LT Li,ZL Gui

2003-01-01

Rare Metal Materials and Engineering

Abstract:High purity BaTiO3 (BT) nano powders with grain size of 100 nm were used to fabricate BT-based BME-MLCCs ceramic materials. The influences of the amount of additives as well as sintering temperatures on the microstructures and dielectric properties of the ceramics were investigated. The BT based MLCC ceramics with average grain size of 100 nmsimilar to200 nm were achieved after sintering below 1240degreesC in reducing atmosphere, showing high dielectric constant more than 2 000, low dielectric loss less than 1%, which could satisfy the X7R characteristics. The inhomogeneous microstructure was also investigated by a transmission electron microscope (TEM) and energy disperse spectrum (EDS).
Microstructural changes and properties of LaxBa(1-x) (Zr0·1Ti0.9)O3 multilayer dielectric ceramics via digital light processing

Liangyi Zeng,Daoyuan Yang,Ziping Li,Wei Xiong,Mingxuan Hao,Haoxuan Ma,Huiyu Yuan,Junyan Cui

DOI: https://doi.org/10.1016/j.ceramint.2024.03.044

IF: 5.532

2024-03-01

Ceramics International

Abstract:Tape casting is currently the mainstream method for preparing multilayer ceramic capacitor (MLCC). However, digital light processing (DLP) shows great promise for MLCC preparation due to its planar exposure and layer-by-layer printing characteristics. In this study, LaxBa(1-x) (Zr0.1Ti0.9)O3 (LBZT) ceramics were fabricated using DLP molding. The effects of La content change on the phase composition, microstructure, and properties of the materials were investigated. A stable ceramic slurry was formulated, and its rheological behaviors and cure properties were studied. TG-DTG was used to develop a two-step debinding process, and its debinding mechanism was analyzed. Finally, the samples were sintered by holding at 1300 °C for 4 h. The results showed that with the increase in La content, the phase composition gradually transformed from the rhombohedral to the tetragonal phase. The microstructure was initially gradually dense, and then the pores increased rapidly, resulting in a quick decrease in relative density. LBZT ceramics exhibited the densest structure at x = 0.006: ρ = 5.79 g/cm3 with a relative density of 95.74%, and have the most excellent dielectric properties (25 °C, 1 kHz): εr = 7068, tanδ = 0.232.

materials science, ceramics
Fabrication of Batio3-Based Dielectrics for Ultrathin-Layer Multilayer Ceramic Capacitor Application by A Modified Coating Approach

Zhibin Tian,Xiaohui Wang,Yichi Zhang,Tae-Ho Song,Kang Heon Hur,Longtu Li

DOI: https://doi.org/10.1143/jjap.50.025801

IF: 1.5

2011-01-01

Japanese Journal of Applied Physics

Abstract:The development of multilayer ceramic capacitor (MLCC) with base metal electrode (BME) requires precise controlling of the microstructure in a very thin dielectric layer (<1 µm). In this paper, a modified coating approach for high coverage of BaTiO3powder for further MLCC application has been developed. The well dispersed and coated BaTiO3powders are prepared and the relative mechanism has been discussed. Furthermore, the ultrafine grained X7R dielectric ceramics were produced by both conventional mixing and modified coating methods. Compared with the conventional mixing method, the ceramics prepared by the coating approach exhibited better TCC (the temperature coefficient of capacitance) performance, with dielectric constant over 2000 and grain size below 150 nm. In addition, it is found through the coating method the content of additives can be reduced to a relatively smaller amount than that required in conventional mixing method.

Design, Fabrication and Dielectric Properties in Core–double Shell BaTiO3-based Ceramics for MLCC Application

Modeling of the Core-Shell Microstructure of Temperature-Stable Batio3 Based Dielectrics for Multilayer Ceramic Capacitors

Formation of Core‐Shell Structure in Ultrafine‐Grained BaTiO3‐Based Ceramics Through Nanodopant Method

Core-shell structure in nanocrystalline modified BaTiO3 dielectric ceramics prepared by different sintering methods

Dielectric Performance and Conductive Mechanism of KNN-based Ceramics Prepared Via Sol–gel Core–shell Process

Effects of Processing on Microstructure and Dielectric Properties of Ultrafine- Grained Barium Titanate Based Ceramics for BME-MLCC Applications

High DC-Bias Stability and Reliability in BaTiO3-Based Multilayer Ceramic Capacitors: the Role of the Core-Shell Structure and the Electrode

Microstructures and Dielectric Characteristics of Ultrafine-Grained Barium Titanate-Based Ceramics for Base-Metal-Electrode Multilayer Ceramic Capacitors Applications

Influence of Sintering Temperature on Core–shell Structure Evolution and Reliability in Dy Modified BaTiO3 Dielectric Ceramics

Exceptional Dielectric Performance of MLCCs Enabled by Defect-Engineered BaTiO3

Boosting Effective Capacitance of Nano-Grained Batio3-Based Ceramics Via a Precise Core-Shell Structure Optimization Strategy

High DC-Bias Stability and Reliability in BaTiO 3 -Based Multilayer Ceramic Capacitors: The Role of the Core-Shell Structure and the Electrode

Medium Temperature Sintered BaTiO3-based Ceramics for X8R Capacitors

Defect Control of Yb-doped Dielectric Ceramics on Improving the Reliability for MLCC Application

Preparation of Nano BaTiO3-Based Dielectric Ceramics by Different Sintering Methods

Diffusion and Defect Chemistry of Temperature-Stable BaTiO3-based Ceramics: Experiment and Theoretical Calculations

Nb-doped BaTiO3-(Bi0.5Na0.5)TiO3ceramics with Core-Shell Structure for High-Temperature Dielectric Applications

Fabrication of BaTiO 3 nanopowders with high tetragonality via two-step assisted rotary furnace calcination for MLCC applications

Ultrafine grained BaTiO3 based ceramic material for temperature stable BME MLCCs

Microstructural changes and properties of LaxBa(1-x) (Zr0·1Ti0.9)O3 multilayer dielectric ceramics via digital light processing

Fabrication of Batio3-Based Dielectrics for Ultrathin-Layer Multilayer Ceramic Capacitor Application by A Modified Coating Approach