Dielectric Performance and Conductive Mechanism of KNN-based Ceramics Prepared Via Sol–gel Core–shell Process

Zhou Yu,Fang Bijun,Zhang Shuai,Lu Xiaolong,Ding Jianning

DOI: https://doi.org/10.1007/s10854-022-08077-0

2022-01-01

Journal of Materials Science Materials in Electronics

Abstract:0.95(Li0.02Na0.50K0.48)(Nb0.95Sb0.05)O3–0.05AgTaO3@BaZrO3 (LNKNbSAT@BZ) lead-free ceramics were prepared via a sol–gel core–shell process, in which the LNKNbSAT core particles with 150–200 nm were prepared by solid-phase method and the “BaZrO3” shell with 5–6 nm was prepared by sol–gel technique. The sol–gel core–shell process synthesized LNKNbSAT@BZ powders exist in submicron and present uniform distribution of elements, which improves reaction activity and reduces calcination temperature. The LNKNbSAT@BZ ceramics calcined at 775 °C and sintered at 1150 °C exhibit pure perovskite phase, large density, and excellent electrical properties, correlating with the coexistence of rhombohedral and tetragonal phases and the sol–gel core–shell process utilized in this work. The LNKNbSAT@BZ ceramics approach to normal ferroelectrics with partially diffused phase transition characteristics proved by the Curie–Weiss law and the exponential law fitting simultaneously. The LNKNbSAT@BZ ceramics show thermal activation relaxation behavior, and the high-temperature Cole–Cole impedance performance can be fitted well by the two equivalent circuits (RQC) connected in series. Such space charges effect conforms to the Arrhenius relationship, which presents a hopping-type process and relates to oxygen vacancies produced by the evaporation of alkali metals during sintering.