Abstract:Ultrafine ceramic powders with high tetragonality are essential for next-generation multi-layer ceramic capacitors (MLCC). The solid-state reaction synthesis commonly used in industry is challenging to prepare ultra-fine BaTiO 3 powders due to issues of the coarse crystallization at high temperature calcinations. In this study, a two-step calcination combining with the rotary furnace was innovatively used to synthesize ultra-fine BaTiO 3 powders with uniform particle and high tetragonality. Through the reaction kinetics study, it was found that the rotary furnace increases the point contact area of Ba 2+ and Ti 4+ by improving the heat transfer efficiency of the solid-phase reaction and decreases the diffusion rate of both, so that the diffusion-nucleation-growth rate is greater than the decomposition rate of BaCO 3 to improve the tetragonality of BaTiO 3 powders. The optimal process parameters were determined and the reaction mechanism was studied. Particularly, the optimized two-step assisted rotary furnace calcination had succeeded in preparing finer powders with an average particle size of 250 nm and tetragonality ( c / a ) of 1.0096. The BaTiO 3 ultrafine powders sintered at 1200 °C has a ceramic density of 96%, dielectric constant of 9173 at the Curie temperature point (131 °C) and a grain activation energy of 0.821 eV, representing excellent dielectric properties and reliability.

Fabrication of BaTiO 3 nanopowders with high tetragonality via two-step assisted rotary furnace calcination for MLCC applications