Comparison of plasma sprayed NbB2-NbC coatings obtained by ex-situ and in-situ approaches

Xiao-long Wang,Yu-xuan Shao,Ming-yan Guo,Yong Yang,Yu-duo Ma,Yu-hang Cui,Wen-wei Sun,Yan-chun Dong,Dian-ran Yan
DOI: https://doi.org/10.1016/j.jeurceramsoc.2021.04.021
IF: 5.7
2021-08-01
Journal of the European Ceramic Society
Abstract:<p>NbB<sub>2</sub>-NbC composite coatings were fabricated on the surface of TC4 by plasma spraying NbB<sub>2</sub>-NbC and Nb-B<sub>4</sub>C composite powders. The microstructure and properties of the as-prepared coatings were investigated, and the reaction mechanism of the Nb-B<sub>4</sub>C composite powder in the plasma jet and the formation mechanism of the NbB<sub>2</sub>-NbC coatings were revealed. During the plasma spraying process, NbB<sub>2</sub>-NbC composite powder underwent melting-depositing and no phase transformation occurred. The formation mechanism of the coating by plasma spraying Nb-B<sub>4</sub>C composite powder was solid phase diffusion-reaction-melting-deposition, and NbB<sub>2</sub> and NbC were formed in situ by the solid phase diffusion reaction between Nb and B<sub>4</sub>C in the plasma jet. The coating obtained by reactive plasma spraying Nb-B<sub>4</sub>C composite powder has obvious lamellar structure, low porosity, high density, higher microhardness, good toughness, and better wear resistance compared with the coating prepared by NbB<sub>2</sub>-NbC composite powder, which is attributed to the exothermic reaction between Nb and B<sub>4</sub>C.</p>
materials science, ceramics
What problem does this paper attempt to address?