Abstract:For improving the wear resistance of Al-30Si-5Cu coating, in this study, the composite coating in-situ synthesized TiC-TiN-TiN 0.8 C 0.2 /Al-30Si-5Cu (TiCN/Al-30Si-5Cu) was prepared used TiH 2 -graphite aggregates as raw materials and plasma spraying technology. The effect of in-situ synthesized ceramic reinforcements on the coating was researched in detail. The results showed that during the plasma spraying process, TiH 2 decomposed and chemically reacted with graphite to form TiC. Additionally, some Ti also reacted with N 2 and O 2 in the air to form TiN and TiO 2 . The phases composition of TiCN/Al-30Si-5Cu composite coating were α-Al, β-Si, θ-Al 2 Cu, β-Ti, TiC, TiN, TiN 0.8 C 0.2 , TiO 2 , as well as amorphous CN X and residual graphite. The TiC-dominated ceramic phases and β-Si were uniformly distributed in the coating, which were tightly bound to the α-Al matrix. Because of the exceptionally rapid cooling rate during the coating preparation, a minor amount of submicron Si particles were also generated. The microhardness, elasticity modulus, and fracture toughness of TiCN/Al-30Si-5Cu composite coating appeared improvements compared to those of Al-30Si-5Cu coating. The TiCN/Al-30Si-5Cu composite coating exhibited smoother friction coefficient curve, along with lower friction coefficient and wear volume in comparison to the Al-30Si-5Cu coating. This suggested that the ceramic reinforcing phases in-situ synthesized led to a notable advancement in the wear resistance of the TiCN/Al-30Si-5Cu composite coating. The wear resistance of TiCN/Al-30Si-5Cu composite coating demonstrated an increasement of 78.3 % over the substrate and 28.2 % over the Al-30Si-5Cu coating. Under the dry friction test conditions outlined in this study, the wear mechanism of the TiCN/Al-30Si-5Cu composite coating included abrasive wear and fatigue wear, coupling with a minimal amount of oxidative wear.

Influence of graphite additive on microstructure and mechanical characteristics of plasma sprayed TiB2–TiC composite coating

Microstructure and properties of CrB2-Cr3C2 composite coatings prepared by plasma spraying

In-situ TiC-Ti5Si3-SiC composite coatings prepared by plasma spraying

Plasma sprayed TiC–Ti5Si3–Ti3SiC2 composite coatings from Ti–SiC-graphite powders with different SiC particle size

The Effect of Powder Preparation Method on the Corrosion and Mechanical Properties of TiN-based Coatings by Reactive Plasma Spraying

Microstructure and Wear Resistance of Grx-Ti-BN Composite Coating on TC4 by Argon Arc Cladding

Properties of Reactive Plasma Sprayed Tib2-Tic0.3n0.7 Based Composite Coatings with Cr Addition and Laser Surface Treatment

Fabrication of plasma-sprayed TiC-Ti5Si3-Ti3SiC2 composite coatings from the annealed Ti/SiC powders

TiC-TiSi2-Al2O3 composite coatings prepared by spray drying, heat treatment and plasma spraying

Microstructure evolution and mechanical properties of reactive plasma sprayed Ti3SiC2–Ti5Si3–TiC composite coatings

Microstructure and properties of Al2O3–ZrO2–TiO2 composite coatings prepared by plasma spraying

Microstructure and properties of in-situ ZrB2-ZrC composite coatings by plasma spraying

Deposition of Ti(C, N)-TiB2 Composite Coating by Reactive LPPS

Effect of the Structure of TiB2–(Fe–Mo) Plasma Coatings on Mechanical and Tribotechnical Properties

Microstructure and Tribological Property of TiC-Mo Composite Coating Prepared by Vacuum Plasma Spraying

Two-scale TiB/Ti64 Composite Coating Fabricated by Two-Step Process

Microstructure and tribological properties of Al-30Si-5Cu composite coating reinforced with ceramic phases synthesized in situ by plasma spraying

Effects of Ti Addition on Microstructure and Tribological Properties of in Situ Composite Carbide Coating WC-TiC/FeNi Fabricated by Plasma Transferred Arc Metallurgical Reaction

Effect of Chromium Carbide Addition on the Microstructures and Properties in Dual Carbide Phases Reinforced Ni-Based Composite Coatings by Plasma Cladding

Effect of TiB2 Content on Properties of Nickel-Coated Graphite Self-Lubricating Coating Prepared by Laser Cladding

Effect of Dispersed TiC Content on the Microstructure and Thermal Property of Shrouded-Plasma-Sprayed FeAl/TiC Composite Coatings