Abstract:A Co-Ni-Cu multiprincipal element alloy (MPEA) powder was successfully synthesized through coprecipitation. Results of energy dispersive spectroscopy (EDS) and X-ray fluorescence spectroscopy (XRF) revealed nearly equal atomic ratios for Co, Ni, and Cu in the Co-Ni-Cu MPEA powder. Moreover, X-ray diffraction (XRD) confirmed a single-phase face-centered cubic (fcc) structure in the Co-Ni-Cu MPEA powder. To explore the differences in microstructure and mechanical properties, we compared a novel WC-2Co-2Ni-2Cu cemented carbide, utilizing the Co-Ni-Cu MPEA as a binder, with conventional WC-6Co and WC-3Co-3Ni cemented carbides prepared via liquid phase sintering. This comparison was conducted using scanning electron microscopy, XRD, and mechanical properties testing. Observations revealed that the surfaces of WC grains in WC-2Co-2Ni-2Cu and WC-6Co appeared smooth and flat, while those in WC-3Co-3Ni exhibited roughness with numerous terraces. In addition, the average grain size was 0.96, 1.14, and 1.22 mu m in WC-2Co-2Ni-2Cu, WC-6Co, and WC-3Co-3Ni, respectively. Notably, the Co-Ni-Cu MPEA inhibited WC grain growth. WC-2Co-2Ni-2Cu (1388 HV30) exhibited hardness similar to that of WC-6Co (1406 HV30) but the highest fracture toughness (9.04 MPa center dot m(1/2)), while WC-3Co-3Ni (1332 HV30) presented the lowest hardness. Bending strength values were recorded at 2406 MPa for WC-2Co-2Ni-2Cu, 2816 MPa for WC-6Co, and 2645 MPa for WC-3Co-3Ni, with WC-6Co exhibiting the highest bending strength. Considering their microstructures, physical properties, and mechanical properties comprehensively, the novel cemented carbides exhibited only slightly reduced bending strength compared to conventional counterparts. Thus, the Co-Ni-Cu MPEA binder demonstrates promising potential as a replacement for the conventional Co metal binder.

Preparation and Properties of WC-TiC-Ni Cemented Carbide

Influences of Ni/Cu/Cr3C2 Composite Additive on Microstructure and Properties of WC–10Co Fine Grained Hardmetal

Enhanced the Mechanical Properties and Corrosion Resistance of Ultra-Coarse Grain WC-8Co Cemented Carbides by the Introduction of Cu and Ni

Preparation of low binder WC-Co-Ni cemented carbides with fine WC grains and homogeneous distribution of Co/Ni

Novel WC-Co-Ti3SiC2 cemented carbide with ultrafine WC grains and improved mechanical properties

Microstructures and Properties of WC-10 wt.%CoCrFeNiAlx Composite Cemented Carbides

Preparation of Ultra-Fine WC-Co Cermet and Its Wear Behavior

Peculiarities of Preparation and Properties of Cemented Carbide WC + 20 Mass% Ni with Ultra-Coarse-Grained Microstructure

Microstructures and Properties of a Novel Cemented Carbide Prepared Using a Co–Ni–Cu Multiprincipal Element Alloy As the Binder

Effect of Ni content on the microstructure and properties of WCoB-TiC cermets

Effect of Mo and C Additions on Eta Phase Evolution of WC-13Co Cemented Carbides

Strengthening and toughening of WC-Ni alloys by adding novel (Ti, Hf, Ta, Nb, Zr)(C, N) high entropy powder

The optimization of mechanical property and corrosion resistance of WC-6Co cemented carbide by Mo2C content

Microstructure and Properties Evaluation of WTi(C,N)-06 Cemented Carbide with TaC and NbC

Microstructure and properties of coarse WC-10CoCrFeMnNi cemented carbide by mechanical alloying and hot pressing sintering

Spark plasma sintered WC-Ni cemented carbides with various contents of ZrC nano-powder

Effect of carbon content on the microstructure and properties of Cr-doped WC–15Co cemented carbide

Preparation and organization of W-Ni/TiC composite material

WC-Ni-SiCw Alloys Prepared by Hot-Pressed Sintering

Low temperature pressureless immediate sintering of novel nanostructured WC/Co/NiCrSiB-alloy cemented carbide

Research on Microstructure and Properties of Ultrafine Grained WC-Ni3Al Cemented Carbide