Abstract:This work presents a promising method to fabricate fluorine-free GdBa2Cu3O7-x (GdBCO) films on LaAlO3 (LAO) substrate using a sol-gel technique. The phase transformation during the fabrication process and the influence of sintering parameters including crystallization temperature and oxygen partial pressure on the microstructure and superconductivity were investigated by X-ray diffraction, scanning electron microscopy and high-resolution transmission electron microscopy. The c-axis oriented microstructure of GdBCO films was obtained under the crystallization temperature of 820 °C and oxygen partial pressure of 1.16%. The barium-containing BaCO3 phase can transform into Ba(OH)2, which contributed to the formation of fluorine-free GdBCO. Moreover, scanning transmission electron microscope characterization revealed that stacking defects were formed near the LAO substrate and spread throughout the whole GdBCO matrix with weak superconductivity regions, which acted as effective pinning centers to inhibit flux creep. This resulted in a stronger current-carrying capacity of the GdBCO film than that of YBa2Cu3O7-x (YBCO) film. Finally, a sustainable GdBCO film with the superconducting transition temperature (T c) of 90 K and the critical current density (J c) of 1.23 MA/cm2 (77 K, 0 T) was achieved through a simple and effective fluorine-free sol-gel method.

High Performance GdBa2Cu3O7− Film Preparation by Non-Fluorine Chemical Solution Deposition Approach

Microstructural characterization and superconducting properties of GdBa2Cu3O7-x films prepared by a fluorine-free sol-gel process

Rapid preparation of cobalt doped GdBa2Cu3O7-δ films by non-fluorine chemical solution deposition method

A New Direct Process to Prepare YBa2Cu3O7- films on Biaxially Textured Ag{110}<211>

Chemical Solution Deposition of YBCO Films with Gd Excess

Preparation of YBa2Cu3O7−δ Films by MOD Method Using Trifluoroacetate As Precursor

Carbon Dioxide Controlled Thermal-Decomposition Reactions for Preparation of High Quality YBCO Films Derived from Fluorine-Free Solution

Controlled-Growth of Yba2cu3o7-Delta Film Using Modified Low-Fluorine Chemical Solution Deposition

Rapid Pyrolysis of SmBa2Cu3O7-δ Films in CSD-MOD Using Extremely-Low-Fluorine Solutions

Thickness Effect of Gd2Zr2O7 Buffer Layer on Performance of YBa2Cu3O7−δ Coated Conductors

Controlled-Growth of $\hbox{YBa}_{2}\hbox{Cu}_{3}\hbox{O}_{7-\delta} $ Film Using Modified Low-Fluorine Chemical Solution Deposition

Etching Sr3Al2O6 sacrificial layer to prepare freestanding GBCO films with high critical current density

Epitaxial growth of Gd 2 Zr 2 O 7 /Y 2 O 3 buffer layers for YBa 2 Cu 3 O 7− δ coated conductors

Preparation of Yba2cu3o7-X Superconducting Thin-Films over Large Area Substrates

Yba2cu3o7-Delta Thin-Films with Bao Precipitates

Precursor evolution and growth mechanism of BTO/YBCO films by TFA—MOD process

Microstructures of YBa1.85Eu0.15Cu3O7− Superconducting Films Grown on SrTiO3 and YSZ Substrates

THE COATED SUPERCONDUCTOR FILM OF YBa2Cu3O7-δ PREPARED BY COLLOIDAL PROCESSING

STUDY OF THE PREPARATION OF HIGH Tc SUPERCONDUCTING YBCO THIN FILMS BY A PLASMA-ASSISTED MOCVD PROCESS

Ag Doping Effects of GdBa2Cu3O7-δFilms by Low Fluorine MOD Method

Epitaxial Pb(Zr 0.52 Ti 0.48 ) O 3 /Y 1 Ba 2 Cu 3 O 7- X Heterostructure Prepared by Pulsed Laser Deposition