Abstract:In previously reported low-fluorine MOD-YBCO studies, the lowest F/Ba mole ratio of the precursor solution was 4.5. Further lowering the F/Ba ratio would bring benefits for the environment, thick film deposition, and an understanding of the heat treatment process. On the other hand, the F/Ba ratio must be at least 2 for full conversion of the Ba-precursor to BaF2 to avoid the formation of BaCO3, which is detrimental to the superconducting performance of YBCO films. In this study, a solution with a 2:1 F/Ba mole ratio was developed, and the fluorine content of this solution was approximately only 10.3% of that used in the conventional TFA-MOD method. Attenuated total reflectance-Fourier transform-infrared spectra (ATR-FT-IR) revealed that BaCO3 was remarkably suppressed in the as-pyrolyzed film-and eliminated at 700 degrees C. Thus, YBCO films with a critical current density (J(c)) of over 5 MA cm(-2) (77 K, 0 T, 200 nm thickness) could be obtained on lanthanum aluminate single-crystal substrates. In situ FT-IR spectra showed that no obvious fluorinated gaseous by-products were detected in the pyrolysis step, which indicated that all F atoms might remain in the film as fluorides. X-ray diffraction theta/2 theta scans showed the presence of BaF2-but not of YF3 or CuF2-in films quenched at 400-800 degrees C. The formation priority of BaF2 over YF3 and CuF2 was interpreted by examining the chemical equilibrium of the potential reactions. Our study could enlarge the synthesis window of precursor solutions for MOD-YBCO fabrication, and serve as a foundation for continuously and systematically studying the influence of fluorine content in the precursor solutions.

Carbon Dioxide Controlled Thermal-Decomposition Reactions for Preparation of High Quality YBCO Films Derived from Fluorine-Free Solution

Controlled-Growth of Yba2cu3o7-Delta Film Using Modified Low-Fluorine Chemical Solution Deposition

Low-Vacuum Pyrolysis of YBCO Films by Using Fluorine-Free Metal Organic Chemical Deposition

Controlled-Growth of $\hbox{YBa}_{2}\hbox{Cu}_{3}\hbox{O}_{7-\delta} $ Film Using Modified Low-Fluorine Chemical Solution Deposition

A Low-Fluorine Solution with the F/Ba Mole Ratio of 2 for the Fabrication of YBCO Films

A Low-Fluorine Solution With A 2:1 F/Ba Mole Ratio For The Fabrication Of Ybco Films

In Situ High Temperature Optical Microscopy Study of Phase Evolution in YBa2Cu3O7−δ Films Prepared by a Fluorine-Free Sol–gel Route

Ethanol-based TFA–MOD Method for Preparation of YBCO Films

A New Direct Process to Prepare YBa2Cu3O7- films on Biaxially Textured Ag{110}<211>

Effects of BaCO3 in transient liquid-assisted fluorine-free metal organic deposition on the growth process of YBCO

High Performance GdBa2Cu3O7− Film Preparation by Non-Fluorine Chemical Solution Deposition Approach

Thick $\Hbox{yba}_{2}\hbox{cu}_{3}\hbox{o}_{7-\Delta}$ Superconducting Films by Low-Fluorine Metallorganic Solution Deposition

Effect of precursor stoichiometry on the superconducting properties of fluorine-free sol–gel YBCO thin films

Surface Morphology and Profile Analysis for Five-Layer YBa 2 Cu 3 O 7− Δ Thick Films Prepared by Low-Fluorine Metallorganic Deposition

Preparation of YBCO superconducting thick films On MgO substrates by modified melt growth process

Fabrication And Analysis Of Tri-Layer Yba2cu3 O (7-Delta) Thick Films By Low-Fluorine Mod Method

Microstructural characterization and superconducting properties of GdBa2Cu3O7-x films prepared by a fluorine-free sol-gel process

THE COATED SUPERCONDUCTOR FILM OF YBa2Cu3O7-δ PREPARED BY COLLOIDAL PROCESSING

Microstructure and superconducting properties of (BaTiO3, Y2O3)-doped YBCO films under different firing temperatures

Fluorine-free sol gel deposition of epitaxial YBCO thin films for coated conductors

Artificial Control for Nucleation and Growth Rate of YBa2Cu3O7-δ Coated Conductors Prepared by Low Fluorine Chemical Solution Deposition