Abstract:In previously reported low-fluorine MOD-YBCO studies, the lowest F/Ba mole ratio of the precursor solution was 4.5. Further lowering the F/Ba ratio would bring benefits for the environment, thick film deposition, and an understanding of the heat treatment process. On the other hand, the F/Ba ratio must be at least 2 for full conversion of the Ba-precursor to BaF2 to avoid the formation of BaCO3, which is detrimental to the superconducting performance of YBCO films. In this study, a solution with a 2:1 F/Ba mole ratio was developed, and the fluorine content of this solution was approximately only 10.3% of that used in the conventional TFA-MOD method. Attenuated total reflectance-Fourier transform-infrared spectra (ATR-FT-IR) revealed that BaCO3 was remarkably suppressed in the as-pyrolyzed film-and eliminated at 700 degrees C. Thus, YBCO films with a critical current density (J(c)) of over 5 MA cm(-2) (77 K, 0 T, 200 nm thickness) could be obtained on lanthanum aluminate single-crystal substrates. In situ FT-IR spectra showed that no obvious fluorinated gaseous by-products were detected in the pyrolysis step, which indicated that all F atoms might remain in the film as fluorides. X-ray diffraction theta/2 theta scans showed the presence of BaF2-but not of YF3 or CuF2-in films quenched at 400-800 degrees C. The formation priority of BaF2 over YF3 and CuF2 was interpreted by examining the chemical equilibrium of the potential reactions. Our study could enlarge the synthesis window of precursor solutions for MOD-YBCO fabrication, and serve as a foundation for continuously and systematically studying the influence of fluorine content in the precursor solutions.

Controlled-Growth of Yba2cu3o7-Delta Film Using Modified Low-Fluorine Chemical Solution Deposition

Controlled-Growth of $\hbox{YBa}_{2}\hbox{Cu}_{3}\hbox{O}_{7-\delta} $ Film Using Modified Low-Fluorine Chemical Solution Deposition

A Low-Fluorine Solution With A 2:1 F/Ba Mole Ratio For The Fabrication Of Ybco Films

A Low-Fluorine Solution with the F/Ba Mole Ratio of 2 for the Fabrication of YBCO Films

Artificial Control for Nucleation and Growth Rate of YBa2Cu3O7-δ Coated Conductors Prepared by Low Fluorine Chemical Solution Deposition

Thick $\Hbox{yba}_{2}\hbox{cu}_{3}\hbox{o}_{7-\Delta}$ Superconducting Films by Low-Fluorine Metallorganic Solution Deposition

Carbon Dioxide Controlled Thermal-Decomposition Reactions for Preparation of High Quality YBCO Films Derived from Fluorine-Free Solution

Rapid Pyrolysis of SmBa2Cu3O7-δ Films in CSD-MOD Using Extremely-Low-Fluorine Solutions

Thick REBaCuO Superconducting Films Through Single-Coating of Low-Fluorine Metallorganic Solution

Fabrication And Analysis Of Tri-Layer Yba2cu3 O (7-Delta) Thick Films By Low-Fluorine Mod Method

Fabrication and Analysis of Tri-layer YBa 2 Cu 3 O 7− δ Thick Films by Low-Fluorine MOD Method

Fabrication and Analysis of Tri-layer YBaCu Thick Films by Low-Fluorine MOD Method

Low-Vacuum Pyrolysis of YBCO Films by Using Fluorine-Free Metal Organic Chemical Deposition

Surface Morphology and Profile Analysis for Five-Layer YBa 2 Cu 3 O 7− Δ Thick Films Prepared by Low-Fluorine Metallorganic Deposition

Effects of BaCO3 in transient liquid-assisted fluorine-free metal organic deposition on the growth process of YBCO

Preparation of YBa2Cu3O7−δ Films by MOD Method Using Trifluoroacetate As Precursor

MOD-Derived YBa<sub>2</sub>Cu<sub>3</sub>O<sub>7-δ</sub> Thin Films using a Fast Pyrolysis Process

Chemical Solution Derived YBa2Cu3.3O7-δ/Y2O3(CuO) Multilayers on Oxide Buffered Metallic Tapes

Mod-derived YBa2Cu3O7-δ thin filmsusing a fast pyrolysis process

Effect of precursor stoichiometry on the superconducting properties of fluorine-free sol–gel YBCO thin films

Enhancing superconductivity of ultrathin YBa<sub>2</sub>Cu<sub>3</sub>O<sub>7-δ</sub> films by capping non-superconducting oxides*