Abstract:YBa2Cu3O7-delta (YBCO) coated conductor has been a promising candidate for high-current transportation material in industry, while the critical current (I-c) becomes a limitation for large-scale application. An efficient way to improve I-c is to increase the thickness of YBCO film without much reduction in critical current density (J(c)). Metallorganic solution deposition (MOD) is a traditional method to fabricate YBCO films while it takes time as long as 10 h during the pyrolysis process. In comparison, Low-Fluorine MOD (LF-MOD) method is applied to reduce the pyrolysis time to less than 2 h. In this paper, we successfully obtain YBCO thick films up to 1.7 mu m by double dip coating process using low-fluorine MOD method. Though wrinkles are frequently observed on the surface of the first layer after pyrolysis at 400 degrees C for 0.5 h, the surface of the final double coated YBCO thick film is homogeneous and cracks are hardly found. Further tests show relatively good c-axis orientation and J(c) value of about 10(5) A/cm(2) at 77 K. With an optimization for the pyrolysis and crystallization processes, better superconducting properties of YBCO thick film are expected.

Thick $\Hbox{yba}_{2}\hbox{cu}_{3}\hbox{o}_{7-\Delta}$ Superconducting Films by Low-Fluorine Metallorganic Solution Deposition