Abstract:Thecost-effective and environment-friendly template of LaMnO 3 /epi-MgO/ion beam-assisted deposited (IBAD-)MgO/solution deposition planarized (SDP) Y 2 O 3 /Hastelloy tape was used as the substrate, on which the technique of metal organic chemical vapor deposition (MOCVD) has been applied to depositing 1.2- μ m-thick YBa 2 Cu 3 O 7− x (YBCO) films by modulating the substrate temperature ranging from 750 to 850 ∘ C. The effects of substrate temperature on the preferential orientation, textures, surface morphology, and performance of the YBCO films were systematically investigated. X-ray diffraction and scanning electron microscope revealed that as substrate temperature increased from 750 to 810 ∘ C, the orientation of YBCO films was transferred from the a -axis to the c -axis; meanwhile, the textures were improved and the films became denser. However, as the substrate temperature rose above 810 ∘ C, the composition distributions and textures of YBCO films degraded quickly, and the films were barium-poor with CuYO 2 impurity arising, of which all negatively affected the critical current density ( J c ) of YBCO films. Around 810 ∘ C, the YBCO film was of the best crystallization and microstructure as well as highly epitaxial growth, leading to the highest J c of 1.8 MA/cm 2 at 77 K and self-field.

Preparation of YBa2Cu3O7−δ Films by MOD Method Using Trifluoroacetate As Precursor

Mod-derived YBa2Cu3O7-δ thin filmsusing a fast pyrolysis process

MOD-Derived YBa<sub>2</sub>Cu<sub>3</sub>O<sub>7-δ</sub> Thin Films using a Fast Pyrolysis Process

Study on the growth of YBCO films deposited by rapid pyrolysis process TFA-MOD

Formation and Characterization of YBa2Cu3O7−δ High-Tc Thin Films by MOCVD with Single Mixed Precursor

Surface Morphology and Profile Analysis for Five-Layer YBa 2 Cu 3 O 7− Δ Thick Films Prepared by Low-Fluorine Metallorganic Deposition

Polymer Assisted Thick Single-Layer YBa 2 Cu 3 O 7-Δ Films Prepared with Modified TFA-MOD Method

Study on PEG Assisted TFA-MOD Method for Rapid Fabrication of YBa2Cu3O7−δ Thin Films: Influence of PEG Additive Amount in Precursor Solutions

Fabrication and Analysis of Tri-layer YBa 2 Cu 3 O 7− δ Thick Films by Low-Fluorine MOD Method

Fabrication and Analysis of Tri-layer YBaCu Thick Films by Low-Fluorine MOD Method

Precursor evolution and growth mechanism of BTO/YBCO films by TFA—MOD process

A New Direct Process to Prepare YBa2Cu3O7- films on Biaxially Textured Ag{110}<211>

STUDY OF THE PREPARATION OF HIGH Tc SUPERCONDUCTING YBCO THIN FILMS BY A PLASMA-ASSISTED MOCVD PROCESS

Double-sided Reel-to-reel Metal-Organic Chemical Vapor Deposition System of YBa2Cu3O7-δ Thin Films

Enhancing superconductivity of ultrathin YBa<sub>2</sub>Cu<sub>3</sub>O<sub>7-δ</sub> films by capping non-superconducting oxides*

A Rapid Process of YBa2Cu3O7−δthin Film Fabrication Using Trifluoroacetate Metal–organic Deposition with Polyethylene Glycol Additive

Preparation of Superconducting Yba2cu3o7-X Films on Metallic Substrates by Pulsed Laser Deposition

Epitaxial Growth of Mocvd-Derived Ybco Films by Modulation of Cu(Tmhd)(2) Concentration

Temperature-Modulated Growth of MOCVD-Derived YBa2Cu3O7−x Films on IBAD-MgO Templates

Study on the growth of YBCO films deposited by TFA-MOD method

Ethanol-based TFA–MOD Method for Preparation of YBCO Films