Abstract:The Ag/BiFeO3 thin films were prepared on ITO/glass substrate by in situ sol–gel method. The morphology and formation of the perovskite phase and Ag nanoparticles (NPs) were studied by XRD, SEM, and UV–Vis spectra. The doping of Ag+ ions and the formation of defects were analyzed by XPS measurement. The dielectric and magnetic properties were measured by impedance analyzer and magnetic property measurement system. Results showed that a few Ag+ ions (<7%) were doped into the bismuth ferrite lattice to substitute Bi. In addition, most of the Ag+ ions were reduced to Ag NPs in BiFeO3 thin films and the Ag NPs/BiFeO3 composite thin film was formed. The Ag+ ions doping was beneficial for not only the formation of crystalline phase of bismuth ferrite, but also the preferential orientation growth of (012) lattice plane. The Ag NPs dispersed in the thin film introduced the percolation behavior into composite the thin film, having the theoretical percolation threshold of f c = 0.131. When the volume fraction of Ag NPs is about 0.12 (Ag/Fe = 0.6). The dielectric constant of the Ag NPs/BiFeO3 thin film reached about 173, being three times as large as that of BiFeO3 thin film without Ag NPs. The minimum value of the dielectric loss was about 0.1–0.2. The typical ferromagnetic property was maintained although the magnetizations decreased a little with the increase in Ag content. The coercive force was 111Oe, showing no typical difference between the thin films with and without Ag NPs. They were beneficial to be used as a candidate in devices with both dielectric and ferromagnetic properties at the same time.

Ag Doping Effects of GdBa2Cu3O7-δFilms by Low Fluorine MOD Method

Ag Doping Effects on Y0.5Gd0.5Ba2Cu3O7−δmultilayers Derived by Low-Fluorine Metalorganic Solution Deposition

THE EPITAXIALLY GROWTH AND GD DOPING EFFECT OF YBa2Cu3O7-δ SUPERCONDUCTING THIN FILMS BY LOW-FLUORINE MOD METHOD

AG DOPING EFFECTS OF YBCO BY LOW FLUORINE MOD METHOD

Co-doping effects of Gd and Ag on YBCO films derived by metalorganic deposition

Microstructural characterization and superconducting properties of GdBa2Cu3O7-x films prepared by a fluorine-free sol-gel process

Effects of Ag Doping on the Critical Current Density of YBa2Cu3O7−y

Influence of Ag Doping on Thermal Conductivity and Magnetic Levitation of Single Grain Ybco Superconductors for High-Temperature Superconducting Maglev

Effect of Ag Doping on the Formation and Properties of Percolative Ag/BiFeO 3 Composite Thin Film by Sol–gel Method

Fabrication and Analysis of Tri-layer YBa2Cu3O7−δ Thick Films by Low-Fluorine MOD Method

Fabrication and Analysis of Tri-layer YBa 2 Cu 3 O 7− δ Thick Films by Low-Fluorine MOD Method

EFFECTS OF <font>Gd</font> DOPING IN <font>YBa</font><sub>2</sub><font>Cu</font><sub>3</sub><font>O</font><sub>7-delta</sub> ON THE CRITICAL CURRENT DENSITY

Chemical Solution Deposition of YBCO Films with Gd Excess

Enhanced performance of GdBCO bulk superconductors by doping a new kind of YGdBa4CuNbOy nanoparticles

Rapid preparation of cobalt doped GdBa2Cu3O7-δ films by non-fluorine chemical solution deposition method

High Performance GdBa2Cu3O7− Film Preparation by Non-Fluorine Chemical Solution Deposition Approach

Effect of Hf Addition on Critical Current Density of (y,eu)ba 2 Cu 3.6 O 7-Δ Thin Films Prepared by Trifluoroacetate Metal Organic Deposition

Fabrication And Analysis Of Tri-Layer Yba2cu3 O (7-Delta) Thick Films By Low-Fluorine Mod Method

Chemical Doping Effect on the Crystal Structure and Superconductivity of Mgb2

Effects Of Gd Doping In Yba2cu3o7-Delta On The Critical Current Density

Property Improvement of 600-Nm-thick YBCO Superconducting Films Fabricated Using a Pb-Modified MOD Method