Abstract:In this study, three different types of ZrO2 films were prepared with different precursors and additives using the sol-gel method. High-temperature annealing was implemented to investigate the impact of temperature on optical properties, microstructure, surface morphologies and absorption of these films. According to the laser-induced damage threshold (LIDT) tests on films having experienced annealing and those implemented with in-situ high temperature, the ZrO2 film with ZrOCl2·8H2O as the precursor and copolymer of silicone and polyaldoxyl ether as the additive had the highest resistance to laser-induced damage. After annealing at 623 K, its LIDT was 21.4 J/cm2, while that at an in-situ high temperature of 523 K was 23.9 J/cm2. The strong high temperature resistance was likely attributed to the usage of carbon-free precursor and high temperature-resistant additive, which contributed to low carbon contents and less structural damage caused by organic matter evaporation. In this context, there were less high temperature-induced impurity and structural defects, leading to higher LIDT values. This study provided a novel method for preparing high temperature-resistant sol-gel films, which shed light upon wider potential application of sol-gel films at high-temperature conditions.

Preparation of Sol-Gel Zro(2)/Sio(2) Multi-Layer Film Based on Uv-Irradiation Treatment

Preparation of ZrO_2/SiO_2 Multilayer Films Via Chemical Methods

Effect of UV-Irradiation on Sol-Gel Optical Films

Infiltrating Between ZrO2 and SiO2 Sol-Gel Films

The preparation of silica-based SiO2-ZrO2 films as waveguides by sol-gel process

Preparation of Sol–gel ZrO2–SiO2 Highly Reflective Multilayer Films and Laser-Induced Damage Threshold Characteristic

Preparation and Study of UV-Absorbing Multi-Layer Films

PREPARATION OF OPTIC FILM WITH HIGH REFRACTIVE INDEX BY CHEMICAL METHODS

Characterization and optical propagation loss of sol-gel derived TiO2/SiO2 films

Preparation and characterization of ZrO2–SiO2 binary films for planar optical waveguides

Preparation and Thermochromic Properties of Sol-Gel-derived Zr-doped VO 2 Films

Preparation of Zirconia Thin Films Via Sol-Gel Process from Inorganic Precursor

Fabrication of Relief Gratings on High Photosensitive SiO 2 /zro 2 Gel Film by UV Exposure

ZrO2 thin films and ZrO2/SiO2 optical reflection filters deposited by sol–gel method

Sol–gel Preparation and Characterization of Nanoporous ZnO/SiO2 Coatings with Broadband Antireflection Properties

Preparation of Sol-Gel ZrO2 Films with High Laser-Induced Damage Threshold under High Temperature

The Research of Micro-structure on ZrO2 Photosensitive Gels Film by UV Exporsure

Pretreating Temperature Controls on Structural, Morphological and Optical Properties of Sol–gel ZnO Thin Films

Microwave Dielectric Properties and Optical Transmittance of SrTiO3/ZnTiO3 Heterolayer Thin Films Fabricated by Sol–gel Processing

Fabrication of SiO2 and SiO2-ZrO2 gel glasses by non-hydrolytic sol-gel process

Preparation of Zirconia/Organosilicone Thin Film by Sol-Gel Method