Abstract:The Schottky barrier height (SBH) variation and its dependence on applied voltage for NiSi/n-Si Schottky diodes with different SBH inhomogeneities have been studied by temperature-dependent current–voltage technique. The results show that the effective barrier height is strongly dependent on the SBH inhomogeneity and the applied voltage. The reduction of effective barrier height increases as the bias varies from forward to reverse, indicating that the pinch off, or more precisely saying, the presence of saddle point in the depletion region, does strongly affect the current transport. Under low reverse bias, the SBH reduction is proportional to one-fourth power of the band bending, which indicates that strip-like SBH inhomogeneity rather than patch-like SBH inhomogeneity exists in our samples. The strip region parameter ω is determined to be 1.63×10−3 and 3.21×10−3V−1/2cm−1/2 for the two diodes respectively. Under high reverse bias, the SBH reduction shows different behaviours for diodes with different SBH inhomogeneity. For diodes with small inhomogeneity, the SBH reduction increases faster than the one-fourth power of the band bending while for diodes with large inhomogeneity, the reduction increases more slowly than in the low reverse bias region. The reason is also explained in term of pinch off.

Ni/Si Solid Phase Reaction Studied by Temperature-Dependent Current-Voltage Technique

Schottky Barrier Height Inhomogeneities of Nickel Mono-Silicide/N-Si Contact Studied by I-V-T Technique

I – V – T Studies on Ni-silicide/n-Si(100) Contacts Formed by Ti–Ni–Si Solid State Reaction

I-V-T studies on ternary silicide Co1-xNixSi2/n-Si Schottky contacts

Thermal stability, phase and interface uniformity of Ni-silicide formed by Ni–Si solid-state reaction

Schottky Barrier Characteristics of Ternary Silicide Co1−xNixSi2 on N-Si(1 0 0) Contacts Formed by Solid Phase Reaction of Multilayer

Effects of the Annealing Temperature on Ni Silicide/n-Si(100) Schottky Contacts

Study of Ni/Si(100) solid-state reaction with Al addition

The material characterization of nickel germanosilicides on SiGe/Si substrate and the contact size effect on Schottky diodes

Solid-Phase Reaction Between Co, Ni/n-poly-Si0.84Ge0.16 and Schottky Barrier Properties of the Formed Contacts

Schottky Contact Properties of Ni/n-poly-Si0.87Ge0.13/n-Si(100) Heterostructure

Electrical Characterization of Nisi/Si Interfaces Formed by A Single and A Two-Step Rapid Thermal Silicidation

The Modulation of Schottky Barrier Height of NiSi/n-Si Schottky Diodes by Silicide As Diffusion Source Technique

Study of Ni/Si(1 0 0) solid-state reaction with Y addition

Voltage dependence of effective barrier height reduction in inhomogeneous Schottky diodes

Study of Ni/Si(100) solid-state reaction with Y addition

Study of Schottky barrier height modulation for NiSi/Si contact with an antimony interlayer

Electrically Active Defects in Ni-Si Silicide Studied by Deep-Level Transient Spectroscopy

Comparison between the solid state reaction of ultrathin Ni and Ni/Ti with Si nanowire on silicon-on-insulator

In-Situ Observation of the Formation of NiSi/Ni<sub>2</sub>Si Heterojunction in SiGe Nanowire with Al<sub>2</sub>O<sub>3</sub> Diffusion Barrier Layer

Solid-Phase Reaction And Schottky Contact Properties Of Co/N-Poly-Si0.84ge0.16/N-Si(100)