Abstract:A large deformation-induced isothermal spheroidization (LDIIS) method was developed for fabricating high-quality semisolid billets of 7005 aluminum alloy. 7005 alloy was first deformed severely via one-pass equal channel reciprocating extrusion (ECRE) and then isothermally treated in semisolid state. The effect of extrusion temperature, isothermal treatment temperature and isothermal treatment time on microstructures were investigated. The results showed that semisolid billet with small grain size and large shape factor was fabricated by LDIIS. It exhibited a finer and more spherical microstructure compared to that obtained by direct isothermal treatment of as-cast material. With increasing isothermal time, the grain size and shape factor kept increasing. But extrusion temperature and isothermal temperature had diverse influences on grain size and shape factor. The desirable semisolid billet with the average grain size of 78 μm and shape factor of 0.87 was obtained by ECREed at 400°C and soaked at 610°C for 20 min. The scanning electron microscope and energy dispersive spectroscopy indicated that Cu, Mg and Zn were mainly distributed inside the intragranular droplet and at the grain boundary. Precipitates containing Fe, Mn and Si were located at the grain boundary. The semisolid microstructure evolution of 7005 alloy can be divided into three stages. In the first stage, the low-melting-point eutectic phase melts and new recrystallized grains are produced. In the second stage, the grains grow together, and the spheroidization effect is obvious. In the third stage, the primary solid phase exhibits polarization growth: the large grains become larger and small grains become smaller.

Structural Evolution of LC 4 Alloy in Making Thixotropic Billet by SIMA Method

Effect of Isothermal Process Parameters on Semi-Solid Microstructure of Chip-Based Al–Cu–Mn–Ti Alloy Prepared by SIMA Method

Microstructure Evolution of Am60 Magnesium Alloy Semisolid Slurry Prepared by New Sima

Microstructure and Texture Evolution of 2A12 Aluminum Alloy Semi-Solid Billet Prepared by SIMA Process

Isothermal Semisolid Microstructure Evolution of Compressively Deformed AZ91D Magnesium Alloy Billet

Microstructural Evolution of A356.2 Alloy Prepared by the SIMA Process

Microstructure Evolution and Tensile Properties of In Situ TiB2(p)/Al-Cu Composite Processed by Modified Strain-Induced Melt Activation Method with Equal Channel Angular Pressing Pre-deformation

Microstructure Evolution of 7005 Alloy Semisolid Billets Fabricated by Large Deformation-Induced Isothermal Spheroidization

Mechanical Behavior of LC 4 Alloy in Semisolid State at High Volume Fractions of Solid

Microstructure Evolution of AZ91D Magnesium Alloy Semi-solid Billets Prepared by a New SIMA Method

Effect of compression ratio on microstructure evolution of Mg–10%Al–1%Zn–1%Si alloy prepared by SIMA process

Semisolid Microstructural Evolution Of Equal Channel Angular Extruded Mg-Al Alloy During Partial Remelting

Microstructure Evolution During Remelting of High Solid Fraction ZL101 Alloy

Microstructural evolution of Mg-10Gd-3Y-1Zn-0.4Zr (wt%) alloy prepared by strain-induced melt activation process

Comparison of Microstructural Evolution of 7075 Aluminum Alloy Fabricated by SIMA and RAP

Compound Fabrication Technology of Semi-Solid Billet of Al-Si Alloy Based on SIMA Method

Semi-solid microstructure and its evolution of LC9 aluminum alloys prepared with directly heating-isothermal treatment method

Preparation of semi-solid billet of magnesium alloy and its thixoforming

Preparation and Thixo-forming Characteristics of Mg-Al-Zn Semi-solid Alloy Billets

Effects of Temperature and Time on Microstructural Evolution of Semisolid 5A06 Aluminum Alloy: Preparation of Semisolid Billets in Ellipsoid Solid Phase