Abstract:In this study, the microstructure and tensile properties of selective laser melted AlSi10Mg at elevated temperature were investigated with focus on the interfacial region. In-situ SEM and in-situ EBSD analysis were proposed to characterize the microstructural evolution with temperature. The as-fabricated AlSi10Mg sample presents high tensile strength with the ultimate tensile strength (UTS) of similar to 450 MPa and yield strength (YS) of similar to 300 MPa, which results from the mixed strengthening mechanism among grain boundary, solid solution, dislocation and Orowan looping mechanism. When holding at the temperature below 200 degrees C for 30 min, the microstructure presents little change, and only a slight decrement of yield strength appears due to the relief of the residual stress. However, when the holding temperature further increases to 300 degrees C and 400 degrees C, the coarsening and precipitation of Si particles in alpha-Al matrix occur obviously, which leads to an obvious decrease of solid solution strength. At the same time, matrix softening and the weakness of dislocation strengthening also play important roles. When the holding temperature reaches to 400 degrees C, the yield strength decreases significantly to about 25 MPa which is very similar to the as-cast Al alloy. This might be concluded that the YS is dominated by the matrix materials. Because the softening mechanism counteracts work hardening, the extremely high elongation occurs. (C) 2020 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.

Microstructural Evolution of Al-Si Alloy above Liquidus Temperature during Holding Temperature

Effect of Holding Time on Microstructure of Mg-9Al-1Si Alloy During Semisolid Isothermal Heat Treatment

Effect of Pouring Temperatures on the Microstructure of the Semi-Solid AlSi9Mg Alloy

Effects of Holding Temperature and Time on Semisolid Isothermal Heat Treated Microstructure of AZ61–0·7Si Magnesium Alloy

Microstructure Evolution of Semi-Solid Mg-14Al-0.5Mn Alloys During Isothermal Heat Treatment

Transition from Crystal to Metallic Glass and Micromechanical Property Change of Fe-B-Si Alloy During Rapid Solidification

Behavior of microstructure evolution of ZL205A cast aluminum alloy during semi-solid isothermal annealing process

Effect of Holding Time on the Microstructure of Mg-3Si-1.70Sn Alloy During Semisolid Isothermal Heat Treatment

Microstructural Evolution of Mg9AlZnY Alloy with Vibration in Lost Foam Casting During Semi-Solid Isothermal Heat Treatment

The Influence of Holding Time on the Microstructure Evolution of Mg–10Zn–6.8Gd–4Y Alloy During Semi-Solid Isothermal Heat Treatment

Microstructural Evolution of Mg-4Al-2.5Ca Alloy During Solidification

Effect of melt holding on morphological evolution and sedimentation behavior of iron-rich intermetallic phases in Al—Si—Fe—Mn—Mg alloy

EVOLUTION OF GLOBULAR AND DENDRITIC STRUCTURES IN SOLIDIFICATION OF Al-Si ALLOYS

Influence of Thermal Rate Treatment and Low Temperature Pouring on Microstructure and Tensile Properties of AlSi7Mg Alloy

Microstructure and Element Distribution during Partial Remelting of an Al-4Cu-Mg alloy

Study on the Influences of Different Process Temperatures on Microstructural Evolution of Mg-11%Al-2%Zn-1%Si Alloy Through Isothermal Semi-Solid Treatment

Microstructure evolution of semi-solid billet fabricated by semi-solid isothermal heat treatment of wrought AlSi7Mg aluminum alloy

Interplay of Heat Treatment and Deformation Temperature on the Microstructural Evolution and Mechanical Behavior of SLM AlSi10Mg Alloy

Microstructure evolution and mechanical properties at high temperature of selective laser melted AlSi10Mg

Effect of Cooling Rates on As-Cast Microstructures of Mg-9Al-xSi (x=1, 3) Alloys

The Microstructural Evolution of a Cold Rolled AlSi9Mg Aluminum Alloy after Semi-Solid Isothermal Treatment Process