Microstructural evolution and anisotropic tensile properties of a bimodal 6A02 Al semi-solid billet
Ying Zhang,Jufu Jiang,Ying Wang,Yingze Liu,Minjie Huang
DOI: https://doi.org/10.1016/j.jallcom.2022.164937
IF: 6.2
2022-07-01
Journal of Alloys and Compounds
Abstract:The effects of isothermal temperature and duration on the microstructures and anisotropic mechanical properties of bimodal 6A02 Al semi-solid billets were studied. These semi-solid billets were fabricated by semi-solid isothermal treatment of hot extruded aluminum alloy (SSITHEAA) method. Elongated and equiaxed grains owning different dislocation densities coexisted at 610–650 °C for 5–30 min. With the increase of temperature, the intensities of micro-textures and intragranular dislocation decreased. The average Schmid factors in transverse directions were still larger than those along extruding directions, preliminarily predicting anisotropic features from the perspective of grain orientation. The anisotropic features of bimodal semi-solid microstructures were verified firstly by uniaxial tensile tests in 0°, 45°, and 90° directions, among which 0 ° specimen at 610 °C/ 20 min exhibited the highest tensile strength and ductility (yield strength σy of 103.8 MPa, maximum tensile strength σmax of 286.9 MPa, and elongation δ of 22.0%). Different from microstructures at solid temperatures, recrystallization degraded mechanical strength of semisolid microstructures to some degree once the grain boundaries were soaked with liquid phase. The dislocation strengthening inside the deformed grains and solid solution strengthening were two dominant strengthening mechanisms. Besides, the elongated grains improved the mechanical properties through dislocation pileup inside the grains, "bridging" effect, "necking" effect and decreasing the content of both flaws and liquid phase. The in-plane anisotropy (IPA) factor indicated that the elongation bore the most serious anisotropy. On the whole, the isotropy of 650 °C/20 min billet was the best, and the corresponding IPA values of σy, σmax and δ were 21.9%, 26.2%, and 47.0%, respectively. For 0° specimens, ductile fracture was dominant, but brittle characteristic was increasingly significant for 45° and 90° specimens.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering