Selective laser melting of magnesium alloys: Necessity, formability, performance, optimization and applications
Kun Li,Chen Ji,Shengwen Bai,Bin Jiang,Fusheng Pan
DOI: https://doi.org/10.1016/j.jmst.2022.12.053
IF: 10.319
2023-03-18
Journal of Materials Science and Technology
Abstract:Selective laser melting (SLM), as a rapid prototyping technology, has been widely used to manufacture high-performance metal components with complex structures, which vitally provides a broad platform for the development and application of magnesium alloys. However, the poor laser formability of magnesium alloys has deleterious consequences in the application of SLM processing. This paper discusses the defect formation mechanisms during the SLM process and summarizes characteristics in terms of mechanical properties, oxidation and corrosion resistance. Current optimization schemes are reviewed from both macro and micro perspectives. Firstly, the relationship between process parameters and formability and material properties is clarified, and advanced optimization methods of the design of experiments, physical models, and machine learning are evaluated. Secondly, the effects of alloying elements, composite reinforcement, and post-treatment on the microstructure and properties of the SLMed magnesium alloy are reviewed. Finally, the future application development prospects are envisaged based on the comprehensive review. This work is significantly helpful to a better scientific understanding of SLMed magnesium alloy and puts forward some meaningful guiding opinions for the future work of magnesium alloy manufacturing. A dual-textured wrought Mg-6.5 Zn (wt.%) alloy with limited yield asymmetry (compressive yield strength / tensile yield strength: 0.90) is reported. Approximately 80% of the grains present the standard texture of wrought Mg alloys while the grain orientation is rotated by ≈ 90o perpendicularly to the c axis in the remaining 20%. The deformation mechanisms responsible for this behavior are analyzed on samples deformed in tension and compression up to different strains. Compressive deformation of the grains with the standard texture is accommodated by 〈a〉 basal slip and extension twinning while tensile deformation promotes 〈a〉 basal and non-basal 〈a〉 prismatic and 〈a〉 pyramidal slip, leading to the typical yield asymmetry. However, the rotated grains present the opposite (and much stronger) yield asymmetry because tensile deformation is absorbed by 〈a〉 basal slip and extension twinning while compression deformation requires 〈a〉 basal slip and compression twinning. Thus, the contribution of the 20% rotated grains to the overall mechanical behavior leads to (almost) similar values of the yield strength in tension and compression. This work provides a physical understanding of the deformation behavior of dual-textured Mg alloys, that can be used to develop novel dual-textured Mg alloys with limited yield asymmetry. A novel Ti 40 Nb 30 Mo 30 –C refractory complex concentrated alloy (RCCA) reinforced with in-situ (Ti, Nb)C carbide was fabricated via mechanical alloying (MA) and hot press sintering (HPS). The results showed that the alloy consisted of the BCC crystal-structured solid solution phase (TNM phase) and FCC crystal-structured carbide (Ti, Nb)C with submicron grain sizes of 0.79 μm and 0.62 μm, respectively. The ultra-fine microstructure benefitted from the inhabitation of in-situ (Ti, Nb)C on grain growth. The ab-initio calculations were conducted to study the formation process of in-situ composite carbide (Ti, Nb)C. Here, the lightweight alloy with a density of 7.04 g/cm 3 exhibited promising compressive mechanical properties, such as yield strength of 2550 MPa at room temperature (RT), 1508 MPa at 800 °C, and 485 MPa at 1000 °C. According to the deformation microstructures at RT and 1000 °C, the dislocation-dominated deformation mechanism in TNM phase was invariable at different temperatures. A brittle-to-ductile translation of (Ti, Nb)C was found to happen at around 1000 °C supported by the stress-strain curve and TEM observation. The excellent mechanical properties of the alloy were attributed to the grain boundary strengthening and the strengthening effect of (Ti, Nb)C that hindered the movement of dislocations. The strategy that incorporating in-situ carbides into light RCCA system could broaden and inspire the design of lightweight and high-strength materials. In this study, SiC/Al–Cu nanocomposites were fabricated via simultaneous solid-state alloying of Cu and dispersing of SiC nanoparticles in Al matrix, for the first time. We showed that a complete solid solution of Cu (4.5 wt%) and a uniform dispersion of dense (up to 15 vol%) SiC nanoparticles in Al matrix can be successfully achieved, by accumulative roll-bonding (ARB) of pure Al, Cu and SiC nanoparticles to high cycles. The as-prepared SiC/Al–Cu nanocomposites exhibited excellent mechanical properties at room temperature and at 300 °C. The microhardness and tensile strength of the SiC/Al–Cu nanocomposites were both significantly increased by incorporating Cu solutes and dense SiC nanoparticles, surpassing those -Abstract Truncated-