Microstructure Evolution and Tensile Properties of In Situ TiB2(p)/Al-Cu Composite Processed by Modified Strain-Induced Melt Activation Method with Equal Channel Angular Pressing Pre-deformation

Sen Yang,Kaikun Wang,Zhiren Sun,Qipeng Li,Kang Chen
DOI: https://doi.org/10.1007/s11665-024-10040-5
IF: 2.3
2024-09-25
Journal of Materials Engineering and Performance
Abstract:The aim of this study is to obtain semisolid billet of the 5 wt.% TiB 2(p) /Al-Cu composite with superior thixotropic behaviors using an equal channel angular pressing-strain induced melt activation (ECAP-SIMA) method. The effects of semisolid isothermal treatment (SSIT) on the microstructure evolution of the as-cast composite were investigated. The results indicate that the α -Al grains first partially melted followed by subsequent growth and spheroidization with increasing holding time. Ostwald ripening is the primary coarsening mechanism. However, after heating at 620–630 °C for 20 min, the coalescence mechanism plays a dominant role in grain growth. In addition, the TiB 2 particles distributed at the grain boundaries can inhibit the coarsening of the α -Al grains. The optimal SSIT parameter (630 °C, 10 min) was chosen based on the comprehensive comparison of the microstructure under different SSIT conditions. Three different ECAP techniques were employed as the pre-deformation step for the SIMA method, resulting in the reduction of the average grain size, but increasing the average shape factor. The subsequent SSIT process can help realize the further grain refinement and slightly improve the roundness of α -Al grains in the ECAP-SIMA composite, thereby improving its formability. Moreover, the ECAP-SIMA composite exhibits enhanced tensile properties than those of the as-cast and SSIT composites, attributed to its refined α -Al grains and the uniform distribution of TiB 2 particles.
materials science, multidisciplinary
What problem does this paper attempt to address?