Abstract:Eutectic microstructures are one of the most common solidification patterns in the binary or multi-component alloy systems. Due to the fine periodic microstructures of the eutectic alloys, the commercial applications of the eutectic alloys can improve the mechanical properties of the castings. The solidification mechanism of eutectic alloys has been widely studied by a lot of experimental works and theoretical analysis over the years. Recently, numerical models were used to study the mechanisms of formation of phase patterns and selection dynamics of the lamellar eutectic, such as phase field (PF) and cellular automaton (CA) model, which can promote the development of eutectic growth theory. Based on the existing CA method for binary primary a phase, a modified cellular automaton (MCA) model was developed for the simulation of binary eutectic growth. In this model, the influence of constitutional and curvature undercooling on the interface morphology was considered. The growth rate of eutectic interface was calculated by the solute conservation at the alpha/liquid and beta/liquid interfaces. The model could simulate the phenomenon of overgrowth, splitting and steady state growth of the eutectic lamellar. CBr4-C2Cl6 eutectic transparent alloy was chosen to validate the model. The simulated results showed that the increasing pulling rate lead to a smaller eutectic lamellar spacing, which had a good agreement with the Jackson-Hunt theory and the experimental results from the literature. Eutectic morphology evolution was simulated under a constant pulling rate and temperature gradient, which showed that the stable lamellar structures existed when the initial lamellar spacing was in a finite range between the minimum stable spacing lambda(m) and the limiting maximum stable spacing lambda(M). A smaller initial lamellar spacing would lead to lamellar annihilation. Conversely, a larger initial lamellar spacing could lead to the lamellar nucleation due to the appearance of solute rich concave at the center of the alpha/liquid interface. Meanwhile, the oscillatory instability of the eutectic lamellar was also reappeared by the MCA model. The MCA model was easily extended to 3D, and the lamellar rod transition during directional solidification was simulated, which showed that the ratio of volume fraction of alpha and beta phase was smaller than 1/pi tend to form lamellar rod transition when the initial lamellar spacing was smaller than lambda(m).

Simulation of Eutectic Growth in Directional Solidification by Cellular Automaton Method