Abstract:In this work, the non-uniform corrosion characteristics of steel bars in stressed reinforced concrete beams after accelerated depassivation and seven-year outdoor natural corrosion is analyzed using fractal theory. 3D laser scanning and 3D reconstruction technology are applied to collect the cross-sectional area along the steel bars and obtain the corrosion curves. The non-uniformity of corrosion is analyzed by fractal dimensions which is calculated by variation method. The results indicate that the initial loading level and loading zone have some influence on non-uniform characteristics of steel bars. For an ordinary concrete beam, the increase of load can cause a reduction of fractal dimension of corrosion curves by 5%, which indicates the non-uniformity of corrosion will increase with the increase of load level. The fractal dimension in the bending zone is lower than that in the tension-shear zone, which indicates that corrosion is more non-uniform in bending zone. However, the loading level and loading zone have a slight influence on corrosion level, and the maximum difference of corrosion level caused by load is merely 0.23%. Furthermore, the corrosion level increases with the decrease of fractal dimension, suggesting that the non-uniformity of corrosion increases with the growth of corrosion level. The incorporation of slag powder can help reduce the non-uniformity of corrosion, but the influence on reduction of the corrosion level is about 0.25%. For concrete structures under marine environment, application of slag powder is a good method to slow down the corrosion and reduce the non-uniformity of corrosion.

A study of the elastic moduli of corrosion products using nano-indentation techniques

Experimental Study of the Modulus of Steel Corrosion in a Concrete Port

Study On Modulus Of Rust Applied In Steel Corrosion Induced Concrete Cracking Model

Evaluation of corrosion morphology on mechanical properties of reinforcing steel bars using numerical simulation and simplified analytical model

State-of-art of corrosion-induced cracking of reinforced concrete structures

Use of instrumented indentation testing to study local mechanical properties of 304L SS welded joints subjected to low-cycle fatigue loadings

Study On Distribution Of Steel Corrosion Products In Concrete Structures

Distribution of millscale on corroded steel bars and penetration of steel corrosion products in concrete

Critical thickness of rust layer at inner and out surface cracking of concrete cover in reinforced concrete structures

Experimental Investigation and Design of Corroded Stud Shear Connectors

Mill Scale and Corrosion Layer at Concrete Surface Cracking

EXPERIMENTAL STUDY OF PIEZOMAGNETISM OF PITTING CORROSIONSTEEL BARS UNDER TENSILE FORCE

Mechanical Performance of Corroded Steel Bars in Concrete

On the Penetration of Corrosion Products from Reinforcing Steel into Concrete Due to Chloride-Induced Corrosion

Crack shape and rust distribution in corrosion-induced cracking concrete

Study on Experimental Method and Morphology of Accelerated Non-Uniform Corrosion of Steel Bars

Composition and expansion coefficient of rust based on X-ray diffraction and thermal analysis

Experimental Study on Distribution of Corrosion Products in Corrosion-Induced Cracks in Reinforced Structures

Non-Uniform Distribution of A Corrosion Layer at A Steel/Concrete Interface Described by A Gaussian Model

Fractal Characterization of Non-Uniform Corrosion of Steel Bars in Concrete Beams after Accelerated Depassivation and Seven-Year Natural Corrosion.

Influence of Environment on the Development of Corrosion Product-Filled Paste and a Corrosion Layer at the Steel/concrete Interface