Influence of Environment on the Development of Corrosion Product-Filled Paste and a Corrosion Layer at the Steel/concrete Interface

Yuxi Zhao,Xiaowen Zhang,Weiliang Jin

DOI: https://doi.org/10.1016/j.corsci.2017.03.026

IF: 7.72

2017-01-01

Corrosion Science

Abstract:Corrosion products at the steel/concrete interface of specimens subjected to different environments were examined. The process of generation of the corrosion product-filled paste (CP), including the corrosion products filling in air voids, was observed. The tiny cracks caused by the artificially accelerated corrosion process were observed to favour CP growth. The thicknesses of CP and the corrosion layer (CL), T-CP and T-CL were measured, and the T-CP - T-CL models are established. The T-CP - T-CL models obtained from this experiment and previous ones are compared, and the influence of environment on the T-CP - T-CL models is also discussed.