Abstract:Low-k dielectric materials were prepared by sintering ZSM-5 zeolite powder compacts at temperatures ranged 1200-1300(degrees)C, and the microwave dielectric characteristics were investigated together with the structure evolution during sintering. It was failed to obtain ZSM-5 ceramics by high temperature sintering because the densification could never occur below the tolerable temperature and the ordered porous structure completely collapsed above the tolerable temperature. The structure changed from ZSM-5 zeolite to SiO2-Al2O3 glass at 1240(degrees)C, and finally to SiO2-based cristobalite ceramics above 1275(degrees)C. A low dielectric constant (2.63-2.78) combined with low dielectric loss (< 0.0005 at 18 GHz) and small temperature coefficient of resonant frequency (varied from -18.6 to -8.1 ppm/C-degrees) was achieved in the present materials, and the value of dielectric loss was the lowest one achieved so far in the dielectric materials with a dielectric constant lower than 3. With the structure evolution from ZSM-5 zeolite to SiO2-Al2O3 glass and finally to SiO2-based cristobalite ceramics, the dielectric constant increased from 2.27 to 2.78, while the Qf value indicated a complicated variation tendency, and the higher Qf values were achieved in the amorphous and crystalline states, while significant drop was determined in the partial amorphous state. It should be a great challenge to prepare dense zeolite ceramics without collapse of ordered porous structure, and then the ultra-low dielectric constant materials with high Q could be expected.

Preparation and Microwave Dielectric Properties of Cristobalite Ceramics

Low-fired Fluoride Microwave Dielectric Ceramics with Low Dielectric Loss

Low-Temperature Sintering and Processing of Microwave Dielectric aBaO plus bNb(2)O(5) Ceramics

Microwave Dielectric Properties of Sol-Gel Processed Bi4si3o12 Ceramics and Single Crystal

Low Temperature Sinter-Ability of Microwave Dielectric Ceramics 0.4(Ca<sub>0.61</sub>Nd<sub>0.26</sub>)TiO<sub>3</sub>-0.6(Li<sub>0.5</sub>Sm<sub>0.5</sub>)TiO<sub>3</sub>

Preparation and Microwave Dielectric Properties of Calcite (caco3) Ceramics

A Microwave Dielectric Ceramic with Ultra-low Dielectric Constant Prepared by Reaction Sintering Method

Low-temperature sintering and phase component modulation of 0.95MgTiO3–0.05CaTiO3 microwave dielectric ceramics

Microwave Dielectric Properties and Low Temperature Firing of (1 − X)li2zn3ti4o12 –xli2tio3 (0.2 ≤ X ≤ 0.8) Ceramics with B2O3–CuO Addition

Preparation and properties of low temperature sintered CaO-B 2 O 3 -SiO 2 microwave dielectric ceramics using the solid-state reaction

Low‐temperature Sintering and Thermal Stability of Li2GeO3‐based Microwave Dielectric Ceramics with Low Permittivity

MICROSTRUCTURES AND MICROWAVE DIELECTRIC CHARACTERISTICS OF CERAMICS WITH THE COMPOSITION BAO.ND2O3.5TIO2

Microstructure, Chemical Bond Characteristics, and Dielectric Response of Cr/Sb Co-Doped Molybdate-Based Ceramics at Microwave and Terahertz Frequency

Microwave Dielectric Properties Of Fused Silica Prepared By Different Approaches

Microwave dielectric properties and sintering behaviors of Zn1.8SiO3.8 ceramics

Low‐k Dielectric Materials Derived from ZSM‐5 Zeolite

A low εr and temperature-stable Li3Mg2SbO6 microwave dielectric ceramics

Low-Temperature Sintering and Microwave Dielectric Properties of (ca0.9mg0.1)sio3 Ceramic with Li2co3 Addition

Microwave Dielectric Properties of the Low-Temperature-fired Li2ZnTi3O8–Li2TiO3 Ceramics for LTCC Applications

Microwave Dielectric Properties of Na+-substituted CaMg0.9Li0.2Si2O6 Ceramics

Crystal Structures and Microwave Dielectric Properties of Novel Low Permittivity Ba1-xSrxZnSi3O8 Ceramics