Microstructure, Chemical Bond Characteristics, and Dielectric Response of Cr/Sb Co-Doped Molybdate-Based Ceramics at Microwave and Terahertz Frequency

Zhanbai Feng,Weijia Guo,Hu Li,Jialun Du,Yuping Zhang,Haitao Wu,Guangbin Duan,Zhenxing Yue

DOI: https://doi.org/10.1016/j.ceramint.2023.02.099

IF: 5.532

2023-01-01

Ceramics International

Abstract:In this research, Cr/Sb was co-doped in Ce2Zr3(MoO4)9 ceramic to optimize the microwave dielectrics and explore the intrinsic mechanism. All ceramics were synthesized using the traditional ceramic method to inves-tigate the effects of Cr/Sb on the microstructure, chemical bond characteristics, phonon vibration spectra, and dielectric response at microwave and terahertz frequencies. X-ray diffraction analysis identified that all samples crystallized in a trigonal system, and no additional peaks observed. The dense ceramic was obtained at 875 degrees C based on the observed sintering behaviors. The co-addition of Cr/Sb significantly reduced the dielectric loss in the matrix. Therefore, dielectric parameters were discussed in terms of intrinsic factors. The findings of chemical bond indicate that Zr(Cr/Sb)-O bonds possess a close relationship with microwave dielectric properties, and Cr/ Sb is occupied preferentially on the Zr(1) sites. Infrared spectrum analysis identified that phonon vibration lower than 400 cm-1 contribute 72.1% to the polarization. In our comparison between the infrared spectrum and terahertz time-domain (THz-TD) spectrum, we found that the permittivity extracted by the latter is closer to the observed value. Consequently, the outstanding parameters of epsilon r = 10.53, Qf = 72,656 GHz, tau f =-16.77 ppm/degrees C were obtained in the Ce2[Zr0.98(Cr0.5Sb0.5)0.02]3(MoO4)9 ceramic.