Crystal structure, Raman spectroscopy, metal compatibility and microwave dielectric properties of Ce2Zr3(MoO4)9 ceramics
Liang Shi,Cheng Liu,Huaiwu Zhang,Rui Peng,Gang Wang,Xiaolei Shi,Xueying Wang,Wenwen Wang,Liang Shi,Cheng Liu,Huaiwu Zhang,Rui Peng,Gang Wang,Xiaolei Shi,Xueying Wang,Wenwen Wang
DOI: https://doi.org/10.1016/j.matchemphys.2020.122954
IF: 4.778
2020-08-01
Materials Chemistry and Physics
Abstract:Low temperature sintered Ce2Zr3(MoO4)9 ceramics were synthesized via the conventional solid-state reaction method. Microstructure and microwave dielectric properties were systematically investigated via the assistance of Raman spectroscopy. Pure phase of Ce2Zr3(MoO4)9 with R–3C space group were obtained, as confirmed through the XRD and Rietveld refinement results. The Raman spectroscopy results indicated that the Raman-active vibrations are mainly derived from the Mo–O bonds. The SEM images exhibited that the porosity and grain morphology, as external factors, affected the microwave dielectric properties, along with the internal factors, such as packing fraction. In addition, theτf values were inversely affected by the distortion of the Zr–O polyhedron. The sample sintered at 750 °C exhibited good microwave dielectric properties: εr = 10.05, Q × f = 24,720 GHz (at 11.3 GHz) and τf = -7.1 ppm/°C. The compatibility between Ce2Zr3(MoO4)9 ceramic matrix and silver/copper electrode was also investigated for the first time.
materials science, multidisciplinary