Sintering behaviors and microwave dielectric properties of BaO–MgO–SiO2 ternary ceramics
Li‐Xia Pang,Zhen Fang,Di Zhou,Wei Wang,Zhong‐Qi Shi,Fayaz Hussain,Moustafa Adel Darwish,Tao Zhou,Shi‐Kuan Sun,Qi‐Xin Liang,Ya‐Wei Chen
DOI: https://doi.org/10.1111/ijac.14802
2024-05-24
International Journal of Applied Ceramic Technology
Abstract:In the present work, five compositions in the BaO–MgO–SiO2 ternary system were chosen, and ceramics were prepared using the solid‐state reaction method. Single phases were formed easily for the first four compositions, and BaMgSi3O8 ceramics were found to be a mixture of both BaSi2O5 and MgSiO3, according to X‐ray diffraction results. Among all the compositions, Ba2MgSi2O7 ceramic sintered at 1225°C possesses the highest Qf (Q = 1/dielectric loss = 1/tanδ, f = resonant frequency) value ∼55 010 GHz along with relative permittivity ∼8.0 and temperature coefficient of resonant frequency (TCF) ∼−57.5 ppm/°C. With 3 wt.% BCB (BaO–B2O3–CuO) additions, Ba2MgSi2O7 ceramic was well densified at 950°C with a relative permittivity ∼8.1, Qf value ∼28 920 GHz (at 12.37 GHz) and TCF value ∼‒56.6 ppm/°C. These series ceramics with low relative permittivity values might be good candidates for low‐temperature co‐fire ceramic technology substrate applications.
materials science, ceramics