Microstructure and Dielectric Properties Control of Ba4(Nd0.7Sm0.3)9.33Ti18O54 Microwave Ceramics

Jing Pei,Zhenxing Yue,Fei Zhao,Zhilun Gui,Longtu Li

DOI: https://doi.org/10.1016/j.ceramint.2007.10.018

IF: 5.532

2009-01-01

Ceramics International

Abstract:Microwave ceramics of Ba4(Nd0.7Sm0.3)9.33Ti18O54 with 0–3wt% Ag additions were synthesized by a citrate sol–gel method. The BaO–B2O3–SiO2 glass was also added into the sol–gel derived BNST ceramic powders as sintering aids. The undoped, Ag- and BaBS-doped samples can be sintered at 1250°C, 1150°C and 1000°C, respectively. The microstructure and dielectric properties were then controlled by doping Ag or BaBS glass. Near isoaxial grains with about 250nm and typical columnar grains were obtained for the silver-doped and BaBS-doped samples, respectively. For the <1wt% silver-doped samples, the dielectric constant and Q×f retained unaltered but τf decreased from 9ppm/°C to 1.4ppm/°C. With increasing silver content from 1wt% to 3wt%, the dielectric constant and τf significantly increased but Q×f decreased. For the BaBS-doped samples, both dielectric constant and Q×f decreased but τf increased with increasing BaBS content.