Effects of Silver Doping on the Sol–Gel‐Derived Ba4(Nd0.7Sm0.3)9.33Ti18O54 Microwave Dielectric Ceramics

Jing Pei,Zhenxing Yue,Fei Zhao,Zhilun Gui,Longtu Li

DOI: https://doi.org/10.1111/j.1551-2916.2007.01892.x

IF: 4.186

2007-01-01

Journal of the American Ceramic Society

Abstract:Tungstenbronze‐type Ba 4 (Nd 0.7 Sm 0.3 ) 9.33 Ti 18 O 54 (BNST) microwave dielectric ceramics doped with 0–10 wt% silver (Ag) particles were successfully fabricated by a citrate sol–gel method. The influence of Ag doping on the sinterability, microstructure, bulk conductivity, and dielectric properties of BNST was investigated. The desired tungstenbronze‐type phase was obtained at 900°–950°C. The sintering temperature of BNST decreased to 1100°C with the aid of a small amount of Ag addition (1 wt%). No chemical reaction between the tungsenbronze phase and Ag was detected. The particle size of the powders decreased with increasing Ag content up to 1 wt% and it then increased with a further increase in the Ag content. The dense fine‐grained ceramics with submicrometer grains (∼300 nm) were obtained with 1 wt% Ag addition. The submicrometer‐grained ceramics had excellent dielectric properties of ɛ r ∼81 and Q × f ∼11 000 GHz. Both the dielectric constant and dielectric loss significantly increased with large additions (>3 wt%) of Ag due to the percolation effect.