Effect of Ag on the Sintering and Dielectric Properties Behavior of Bi1.5ZnNb1.5O7 Ceramics

Weihong Liu,Hong Wang,Kecheng Li,Xi Yao

DOI: https://doi.org/10.1016/j.jallcom.2009.10.160

IF: 6.2

2009-01-01

Journal of Alloys and Compounds

Abstract:Bi1.5ZnNb1.5O7–Ag composites were prepared by solid state method. The sintering temperature was lowered to 900°C for the Bi1.5ZnNb1.5O7 ceramics with 3wt% silver doping. The microstructures, surface morphologies, and dielectric properties of the composites were investigated. A small amount of silver doping is shown to promote grain growth. The grain size of the composites sintered at 950°C increased from 2 to 6μm with the silver content increasing from 1 to 4wt%. The composites with 4wt% silver sintered at 950°C had the relative permittivity of 215, and dielectric loss of 10−4 ranging from 100Hz to 1MHz. The silver doping in composites also improves the electrical resistivity of Bi1.5ZnNb1.5O7–Ag composites, and increases the electrical resistivity value from 1013 to 1015Ωcm for the samples sintered at 900 or 950°C by increasing the silver content from 1 to 4wt%. The Bi1.5ZnNb1.5O7–Ag composites with lower loss and larger electrical resistivity would be useful for electronic devices in RF application.