A- and B site cosubstituted Ba 6-3xSm 8+2xTi 18O 54 microwave dielectric ceramics

Xiangming Chen,Yi Li

IF: 4.186

2002-01-01

Journal of the American Ceramic Society

Abstract:Tin (Sn) substitution into the B-site and Nd/Sn cosubstitution into the A- and B-sites were investigated in a Ba 6-3xSm 8+2xTi 18O 54 solid solution (x = 2/3). A small amount of tin substitution for titanium improved the temperature coefficient of resonant frequency (τ f) but led to a decrease of the relative dielectric constant (ε) and the quality factor (Qf). The Ba 6-3xSm 8+2x(Ti 1-zSn z) 18O 54-based tungsten-bronze phase became unstable for compositions with a tin content of ≥10 mol%, where BaSm 2O 4 and Sm 2(Sn,Ti) 2O 7 appeared, and finally, these phases became the major phases. On the other hand, Nd/Sn cosubstitution led to a good combination of high ε, high Qf, and near-zero τ f Excellent microwave dielectric properties were achieved in Ba 6-3x(Sm 1-yNd y) 8+2x(Ti 1-z Sn z) 18O 54 ceramics with y = 0.8 and z = 0.05 sintered at 1360°C for 3 h: ε = 82, Qf = 10 000 GHz, and calculated τ f = +17 ppm/°C. The tolerance factor and electronegativity difference exhibited important effects on the microwave dielectric properties, especially the Qf value. A large tolerance factor and high electronegativity difference generally led to a higher Qf value.