Microwave Dielectric Ceramics Of Ba6-3xnd8+2x(Zryti1-Y)(18)O-54 Solid Solution

Yj Wu,Xm Chen

2001-01-01

Abstract:In order to find a new approach for properties modification in Ba6-3xNd8+2xTi18O54 microwave dielectric ceramics, the effects of partial substitution of Zr for Ti ions were investigated. The sintering characteristics, microstructures and microwave dielectric properties were determined for the composition of BaNd2(ZryTi1-y)(4)O-12 (x=0.5). As the amount of Zr increased, both the densification temperature and the dielectric loss increased, and the dielectric constant decreased. It was found that Zr substitution for Ti had the advantage of improving the temperature coefficient of dielectric constant, when the substitution amount of Zr for Ti ions was below the solid solution limit (between 25mol% and 50mol%) of BaNd2Zr4O12 in BaNd2Ti4O12.