Abstract:The effects of Bi substitution for Nd in Ba 6−3 x Nd 8+2 x Ti 18 O 54 x = 2/3) solid solution upon the microstructures and microwave dielectric properties were investigated. The solid solubility limit of Bi in Ba 6−3 x Nd 8+2 x Ti 18 O 54 x = 2/3) solid solution was about 15 mol%, the same as that for x = 0.5, and densification of the present solid solutions could be performed well at lower temperatures. However, the variation tendency of microwave dielectric properties with composition in the present ceramics quite differed from that for x = 0.5: (1) The temperature coefficient of resonant frequency in the present ceramics showed a continuous variation from positive to negative and did not indicate extreme value at the solid solubility limit. (2) Near-zero temperature coefficient of resonant frequency combined with high-ε and high-Qf values could be obtained in the present ceramics, while that for x = 0.5 had a lower limit of +15 ppm/°C. (3) The dielectric constant also showed a continuous increase for the present compositions, while that in x = 0.5 had an extreme at solid solubility limit. Ceramics with composition of Ba 6−3 x (Nd 0.85 ,Bi 0.15 ) 8+2 x Ti 18 O 54 x = 2/3) showed excellent dielectric properties of ε = 99.1, Qf = 5290 GHz, and τ f = −5.5 ppm/°C.

Dielectric Ceramics of Ba6-3xnd8+2x(Zr,Ti)(18)O-54

Microwave Dielectric Ceramics Of Ba6-3xnd8+2x(Zryti1-Y)(18)O-54 Solid Solution

Effects Of B-Site Substitution On Microwave Dielectric Properties Of Ba6-3xnd8+2x [Ti1-Z (Ni1/3nb2/3)(Z)] O-18(54) Ceramics

Microwave dielectric properties and microstructure of (Ba 0.98 Sr 0.02 ) 3.75 Nd 9.5 Ti 18−x (Zn 1/3 Nb 2/3 ) x O 54 ceramics

Microwave Dielectric Properties of Ba 3.75 Nd 9.5 Ti 18−z Cr 4z/3 O 54 Ceramics

Microwave Dielectric Properties and Microstructure of Ba6−3xNd8+2xTi18−y(Cr1/2Nb1/2)yO54 Ceramics

Structures and microwave dielectric properties of Ba<sub>6-3x</sub>(Nd,Biy)<sub>8+2x</sub>Ti<sub>18</sub>O<sub>54</sub> (x = ⅔) solid solution

Microstructure and Microwave Dielectric Properties of Ba 3.75 Nd 9.5 Ti 18− z (Mg 1/3 Nb 2/3 ) z O 54 Ceramics

A- and B site cosubstituted Ba 6-3xSm 8+2xTi 18O 54 microwave dielectric ceramics

Coordinated Modification Of Microstructures And Properties In Ba6-3xnd8+2xti18o54 Microwave Dielectric Ceramics

Modified Ba6-3xNd8+2xTi18O54 microwave dielectric ceramics

A‐ and B Site Cosubstituted Ba6−3xSm8+2xTi18O54Microwave Dielectric Ceramics

Tin Substitution for Titanium in Ba6-3xnd8+2xti18o54 Microwave Dielectric Ceramics

Microwave Dielectric Properties of BaO–2(1 − X)zno–xnd2o3–4tio2 (x = 0–1.0) Ceramics

Structures and Microwave Dielectric Properties of Ba 6−3 X (nd,bi Y ) 8+2 X Ti 18 O 54 X = 2/3) Solid Solution

Microwave dielectric properties of Ba[(Zn1−xCox)1/3Nb2/3]O3 ceramics

Bismuth/Samarium cosubstituted Ba6-3xNd8+2xTi18O54 microwave dielectric ceramics

Microwave Dielectric Properties Of Ba[(Zn1-Xcox) Nb-1/3(2/3)]O-3 Ceramics

Bismuth/Samarium Cosubstituted Ba6−3xNd8+2xTi18O54 Microwave Dielectric Ceramics

(Cu1/3nb2/3)4+ Ionic Substituting Effects, Low-Temperature Sintering Behaviors, and Improved Temperature Stability of Ba3Nb4Ti4O21 Microwave Dielectric Ceramics

Influence of Bi substitute on structure and dielectric properties of BaO Nd2O3 TiO2 based microwave dielectric ceramics