Abstract:In this paper, we carried out a systematic investigation on gate degradation and the physical mechanism of the Schottky-type <inline-formula xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink"> <tex-math notation="LaTeX">${p}$ </tex-math></inline-formula> -GaN gate HEMTs under positive gate voltage stress. The frequency- and temperature-dependent measurements have been conducted. It is found that the time-dependent gate degradation exhibits weak relevance with frequencies ranging from 10 to 100 kHz under dynamic gate stress and is similar to that in static gate stress. Both the gate breakdown voltage (BV) and mean-time-to-failure (MTTF) show positive temperature dependence. Moreover, the current–voltage ( <italic xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">I–V</italic> ) characteristics and threshold voltage ( <inline-formula xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink"> <tex-math notation="LaTeX">${V}_{\text {TH}}$ </tex-math></inline-formula> ) instability of <inline-formula xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink"> <tex-math notation="LaTeX">${p}$ </tex-math></inline-formula> -GaN devices before/after gate degradation are compared and analyzed. The degraded Schottky junction exhibits an ohmic-like gate behavior. It is revealed that under a large gate bias stress, high-energy electrons accelerated in the depletion region of the <inline-formula xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink"> <tex-math notation="LaTeX">${p}$ </tex-math></inline-formula> -GaN layer would promote the formation of defect levels near the metal/ <inline-formula xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink"> <tex-math notation="LaTeX">${p}$ </tex-math></inline-formula> -GaN interface, leading to the initial <inline-formula xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink"> <tex-math notation="LaTeX">${p}$ </tex-math></inline-formula> -GaN layer degradation. The subsequent high gate leakage density could cause the final degradation of the AlGaN barrier.

The Degradation Mechanism of an AlGaN/GaN High Electron Mobility Transistor under Step-Stress

Multiple Defects Cause Degradation After High Field Stress in AlGaN/GaN HEMTs

High-field-induced Electron Detrapping in an AlGaN/GaN High Electron Mobility Transistor

Analysis of Algan/Gan High Electron Mobility Transistors Failure Mechanism under Semi-On Dc Stress

Electro-thermal-stress interaction of GaN HEMT breakdown induced by high power microwave pulses

Degradation Behavior and Trap Analysis Based on Low-Frequency Noise of AlGaN/GaN HEMTs Subjected to Radio Frequency Overdrive Stress

Electrical Degradation of In Situ SiN/AlGaN/GaN MIS-HEMTs Caused by Dehydrogenation and Trap Effect Under Hot Carrier Stress

Investigation of Gate Degradation Characteristics of AlGaN/GaN HEMTs under PWM Stress

Stress Reliability Study of GaN HEMT Devices

Gate Reliability and its Degradation Mechanism in the Normally OFF High-Electron-Mobility Transistors With Regrown p-GaN Gate

V T Shift and Recovery Mechanisms of p-GaN Gate HEMTs Under DC/AC Gate Stress Investigated by Fast Sweeping Characterization

Frequency- and Temperature-Dependent Gate Reliability of Schottky-Type <inline-formula> <tex-math notation="LaTeX">${p}$ </tex-math></inline-formula>-GaN Gate HEMTs

A Comparative Study on the Degradation Behaviors of Ferroelectric Gate GaN HEMT with PZT and PZT/Al2O3 Gate Stacks

Effect of Electro-Thermo-Mechanical Coupling Stress on Top-Cooled E-Mode AlGaN/GaN HEMT

Recoverable Current Collapse Effect of p-GaN HEMTs Under Short Circuit Stress

Investigation of Bending-Induced Degradation of Flexible AlGaN/GaN HEMTs

Electrical Properties and Reliability of AlGaN/GaN High Electron Mobility Transistor under RF Overdrive Stress at High Temperature

Impact of Hole-Deficiency and Charge Trapping on Threshold Voltage Stability of P-Gan HEMT under Reverse-bias Stress

Degradation Mechanisms of Gate Leakage in GaN-Based HEMTs at Low Dose Rate Irradiation

Analysis of Trap and Recovery Characteristics Based on Low-Frequency Noise for E-Mode GaN HEMTs under Electrostatic Discharge Stress

Current Collapse and High-Electric-Field Reliability of Unpassivated GaN/AlGaN/GaN HEMTs