Analysis on Deposition Mechanism of Ash with High Ash Fusion Temperatures on the Heat-insulation Layer in Boiler

ZHOU Jun-hu,ZHAO Xiao-hui,LIU Jian-zhong,YANG Wei-juan,HUANG Zhen-yu,CEN Ke-fa

DOI: https://doi.org/10.3321/j.issn:0258-8013.2008.14.004

2008-01-01

Abstract:Analysis and experiments were carried out on one case that ash deposited on the heat-insulation layer(refractory) in one boiler burning coal water slurry with high ash fusion temperatures(AFTs)(with initial deformation temperature above 1 400℃).Elemental analysis shows that both iron and calcium are enriched in the three samples corresponding to different stages of deposition,viz.initial,middle and mature stage respectively.In situ visual observation and scanning electron microscope(SEM) morphology indicate that no fusion occurs for the deposits;X-ray diffractometer(XRD) crystallization phase results show that there is no significant difference between each stage deposits.For each stage deposits,mullite,feldspar and some iron mineral form in the deposits.Specific surface area measurements on coal ash samples sintered at different temperatures were performed using nitrogen adsorption(N2-BET),the results show that below the ash deformation temperature,even though no fusion occurs,the specific surface area decreases with increasing temperature,which gives the evidence that sintering does strongly occur below ash deformation temperature.The enrichment of both iron and calcium leads to strong sintering propensity of the deposited particles,and the strength developed by sintering provides forces to prevent deposits from shedding.