Formation of Ash Deposit Within Residual Oil Burning Boilers

ZHOU Jun-hu,ZHAO Xiao-hui,CAO Xin-yu,LIU Jian-zhong,CEN Ke-fa
DOI: https://doi.org/10.3969/j.issn.1674-7607.2007.01.015
2007-01-01
Abstract:Chemical compositions of ash deposited on different heat delivery surfaces of a certain residual oil burning boiler are found to differ from on another according to an analysis of respective samples wherewith their origins of these deposits were revealed.With XRF(X-ray fluorescence) spectroscopy,SEM-EDX(scanning electronic microscopy with energy dispersive X-ray) spectrometetry and XRD techniques,the chemical composition as well as the morphology and mineralogy characteristics were identified.The oil ash was also subjected to a thermal analysis(DCS plus TG) to determine the transition temperature of the minerals contained.Results show that the main crystalline phase of deposited ash in the surface is of the mullite type,while tha tof the oil ash is faujasite.Obvious exothermic peak,observed at 980℃ on the DSC curve,indicates that the main content of oil ash starts to turn into mullite at 980℃,during which large amount of heat is released.This proves that mullite deposits in the radiation heat absorption area mainly comes from additives used in the original oil's cracking stage.Deposits on the second stage(high temperature) superheater surface mainly contaiin mullite(mostly coming from cracking additives),vitreous matter,cristobalite and microcline(potassium aluminosilicate),while those on the first stage(low temperature) superheater and economizer surfaces,consist of sodium vanadate,ferrite vanadate and calcium sulfate,which mainly come from minerals contaiined in the original oil itself and are deposited in the rear part of the boiler after having undergone a conversion under high temperature conditions in the furnace.Figs 3,tables 4 and refs 9.
What problem does this paper attempt to address?