Abstract:WC-Co cemented carbides are widely used in the fields of military, aerospace, mining and cutting industry etc. In this paper, a new two-step method for the preparation of WC-Co cemented carbides was proposed. First, the mixture of yellow tungsten trioxide (WO3) and cobaltic oxide (Co2O3) were reduced by carbon black to remove all the oxygen. Then, the carbothermic reduction products were precisely mixed with an appropriate amount of carbon black to directly prepare WC-Co cemented carbides. The effects of C/WO3 ratio on the phase composition, morphological evolution, particle size and mechanical properties of products are investigated. The experimental results revealed that when the C/WO3 molar ratio was above 2.7, all oxygen in the raw material mixture were removed by carbon black and a mixture of W2C and η-phase were obtained after the first step of carbothermic reduction at 1150 °C for 2 h; then, the mixture of carbothermic reduction product and an appropriate content of carbon black was compacted, and the green compact was first carbonized at 1200 °C for 2 h and then sintered at 1450 °C for 4 h to prepare cemented carbides. With the increase of C/WO3 ratio at the first stage, the content of η-phase with a low melting point increased, which resulted in the large grain size of WC in the finally prepared cemented carbide. Compared with the traditional method of preparing cemented carbides, the cemented carbides prepared by the current method showed a higher hardness and toughness. Furthermore, the addition of a proper content of the VC in the second stage can significantly inhibit the grain growth of WC and further increase the hardness of cemented carbides.

Synthesis of nanocrystalline cubic substoichiometric WC1 − z powders by mechanochemical technology

Mechanosynthesis Mechanism of Tic Powders

Atomic Scale Stability of Tungsten-Cobalt Intermetallic Nanocrystals in Reactive Environment at High Temperature.

Effect of Ball Milling Parameters on Properties of Nano-Sized Tungsten Powder via Mechanochemical Processing

Synthesis of WC-0.67wt.%Cr3C2 nanopowders by a one-step reduction-carbonization method and their characterization

Study on influencing factors and mechanism of high-quality tungsten carbide nanopowders synthesized via carbothermal reduction

Nano-sized Amorphous Cu–Zr Alloy Particles Prepared by Mechanochemical Reaction

Synthesis of Nano Tungsten Carbide Via Loose Yellow Tungsten Oxide Rod Processing

Fabrication of ultrafine and nanocrystalline WC–Co mixtures by planetary milling and subsequent consolidations

Mechanochemical synthesis of sodium tungsten bronze nanocrystalline powders

A Novel Method for Direct Synthesis of WC-Co Nanocomposite Powder

A short and facile process to synthesize WC-Co cemented carbides

Mechanosynthesis of molybdenum carbides by ball milling at room temperature

Preparation of nano-scaled WC powder by low-temperature carbothermic reduction method

Preparation of Ti/Al based nanophase composite powder by mechanical alloying

Effect of ZrC nano-powder addition on the microstructure and mechanical properties of binderless tungsten carbide fabricated by spark plasma sintering

Synthesis and Formation Mechanism of W/TiC Composite Powders by a Wet Chemical Route

Mechanosynthesis of TaC-WC powders under environmental conditions and their consolidation via electric arc furnace

Phase Composition and Microstructure of Binderless Wc-Zrc Cemented Carbides Fabricated by Spark Plasma Sintering

Mechanochemical Synthesis of Entropy-Stabilized Wurtzite Zn (1– x ) (CoMnNiCuMg) x O for RWGS Reaction

Preparation Technology of Ultra-Fine Tungsten Carbide Powders: an Overview