Abstract:The magnetron sputtering technique was employed to prepare Zr-alloyed Cu thin films with Zr addition ranging from 0 to 7.0 at.%. Microstructure evolution with Zr doping was characterized by using the transmission electron microscope and atom probe tomography. Plastic deformation characteristics (hardness, strain rate sensitivity and activation volume) of the Cu-Zr alloyed films were examined by using nanoindentation testing. Significant Zr doping effects on the microstructure were clearly uncovered that (i) the Zr segregated at grain boundaries and tuned the grain boundary structure. With increasing the Zr addition, CuZr amorphous particles at grain boundaries (3.0 at.% Zr) and even three dimensional CuZr amorphous grain boundary network (7.0 at.% Zr) were formed; (ii) the grains (size and morphology) and nanotwins were notably influenced by the Zr doping. In particular, the nanotwin thickness was reduced from similar to 25 nm in the pure Cu film down to 5 nm in the Cu-Zr alloyed films. Accompanied with the microstructure evolution, the Cu-Zr thin films displayed hardness and strain rate sensitivity highly sensitive to the Zr doping, i.e., hardness increasing while strain rate sensitivity decreasing with raising the Zr addition. The strengthening and deformation mechanisms were discussed in terms of the microstructure-property relationship. Three regimes were divided within the studied Zr doping range: grain/nanotwin boundary-dominated strengthening mechanism in the regime I of pure Cu film, dislocation nucleation-controlled nanotwin softening mechanism in the regime II of Zr addition <= 3.0 at.%, and intergranular amorphous layer-mediated strengthening mechanism in the regime III of Zr addition up to 7.0 at.%. In addition, the reduction in strain rate sensitivity with Zr doping was quantitatively described by adopting a model that involves the thermally activated partials depinning mechanism based on the effective dislocation segment length. (C) 2017 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Nano-sized Amorphous Cu–Zr Alloy Particles Prepared by Mechanochemical Reaction

Preparation and microstructure of nano-sized Cu particles by mechanochemical reaction

Nano-sized amorphous alumina particles obtained by ball milling ZnO and Al powder mixture

Bulk Nanostructure Formation Directly From The Multicomponent Alloy Melt

Nanostructured Composite Obtained by Mechanically Driven Reduction Reaction of Cuo and Al Powder Mixture

Microstructure and phase components of the as-cast Cu-0.4%Cr-0.12%Zr-0.01%Si

Amorphous Intergranular Films Enable the Creation of Bulk Nanocrystalline Cu-Zr with Full Density

A Method to Prepare Nano-Sized Copper Particles and Rods on the Surface of Cu Composite Films

Nanocrystalline Composites with High Strength Obtained in Zr–Ti–Ni–Cu–Al Bulk Amorphous Alloys

Reaction Synthesis Of Nano-Scale Zrc Particulates By Self-Propagating High-Temperature Synthesis From Al-Zr-C Powder Mixtures

Study on Microstructure and Properties of Cu-Zr Alloy Prepared by Mechanical Alloying

Self-formed Submicron-Scale Faceted Copper Particles on the Surface of Annealed Cu-Zr Films

Heterogeneous nucleation of β-type precipitates on nanoscale Zr-rich particles in a Mg-6Zn-0.5Cu-0.6Zr alloy

Revealing the High Strength and High Thermal Stability of a Nano-Lamellar Cu-0.1 At. % Zr Alloy

A Low Temperature Mechanochemical Synthesis And Characterization Of Amorphous Ni-B Ultrafine Nanoparticles

Mechanochemical synthesis of nanocrystalline Ni-Zn ferrite

Nanocutting mechanisms of Cu50Zr50 amorphous alloy: A molecular dynamics simulation

Mechanochemical Synthesis of Nanocrystalline Zinc Ferrite

Achieving Tailorable Nano-Crystallization in a Fully Amorphous Zr50Cu42Al8 Alloy

Zr Alloying Effect on the Microstructure Evolution and Plastic Deformation of Nanostructured Cu Thin Films

In Situ Synthesis Of Nano-Sized Zrc And Its Formation Mechanism By Combustion Synthesis From Zr-C-Cu System