Abstract:β‐Si3N4 ceramics with an additive oxide system of 1 wt% MgO and 3 wt% Re2O3 (Re = Gd, La, Y and Yb) were fabricated by liquid phase sintering at 1950°C under nitrogen pressure of 748 kPa. Starting α‐Si3N4 powder with 10 vol% rod‐like β‐Si3N4 seed crystallites and an extended sintering time from 5 to 40 h resulted in the formation of bimodal microstructure composed of fine matrix grains and large grains. The 40 h‐sintered specimens of pseudo ternary β‐Si3N4‐MgO‐Gd2O3 system exhibited enhanced thermal conductivity of 127.2 ± 2.5 W m−1 K−1 associated with a degradation of the fracture strength from 1008.0 ± 38.0 to 491.7 ± 32.0 MPa, which was due to the formation of coarse‐grained aggregates that acted as both fracture origin as well as a thermal conductive pathway. The theoretical thermal conductivity was predicted for the sintered specimens by using equations based on a mean‐field micromechanics model to estimate the effective thermal conductivity of each component of binary composites. The calculation results suggested that the thermal conductivity of the large β‐Si3N4 grains (≥ 2 μm in diameter) was relatively high and estimated to be in the range of 175 to 191 Wm−1 K−1.The improved thermal conductivity of the 40 h‐sintered specimens was further discussed for the series of β‐Si3N4‐MgO‐Re2O3 systems based on the nanostructure characterization results obtained by the high‐resolution transmission electron microscopy and scanning transmission electron microscopy‐energy dispersive X‐ray spectrometry analyses. This article is protected by copyright. All rights reserved

Effects of Rare-Earth Oxide Additions and Heat-Treatment Temperature on the Transformation and Microstructure of Silicon Nitride

The phase transformation behavior of Si3N4 with single Re2O3 (Re = Ce, Nd, Sm, Eu, Gd, Dy, Er, Yb) additive

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

Effect of Rare Earth Additives on Properties of Silicon Nitride Ceramics

The effect of additives on sintering behavior and strength retention in silicon nitride with RE-disilicate

Oxidation behavior and mechanical property of Si3N4 ceramics with rare earth oxide addition

Effects of MgO-RE2O3 and SiO2-RE2O3 (RE = La, Nd, Gd, Ho and Lu) Complex Sintering Additives on the Phase Composition, Microstructure and Mechanical Properties of Dual-Phase Si3N4 Ceramics

Effect of Re2O3–MgO additives on the microstructure evolution and properties of β-Si3N4 ceramics

Mechanical Property and Oxidation Behavior of Self-Reinforced Si3N4 Doped with Re2O3 (Re=Yb, Lu)

Preparation of the Rod-Like Β-Si3n4 Particles Favoring the Self-Reinforcing Si3N4 Ceramics

Direct Measurement of Residual Stresses and Their Effects on the Microstructure and Mechanical Properties of Heat-Treated Si3N4 Ceramics II: with CeO2 As a Single Additive

Phase Evolution in Heat‐Treated Si3N4 with Additions of Yb2O3

The Effects of the Single Additive on the Fabrication of Rod-like β-Si3N4

The effects of the single additive on the fabrication of rod-like beta-Si3N4

Effect of rare earths on mechanical properties and microstructures of Si3N4-based ceramics

Thermal conductivity improvement in Si3N4 ceramics via grain purification

Preparation of the rod-like {beta}-Si{sub 3}N{sub 4} particles favoring the self-reinforcing Si{sub 3}N{sub 4} ceramics

Influence mechanism of rare earth (RE) on inclusion modification in non-oriented silicon steel

Secondary crystalline phases and mechanical properties of heat-treated Si3N4

Microstructure and Performance of Silicon Nitride Ceramics with Lu2O3 Additives

The Fabrication, Mechanical Property And Oxidation Of Si3n4 Ceramics With Rare Earth Oxide Addition