Preparation of the rod-like {beta}-Si{sub 3}N{sub 4} particles favoring the self-reinforcing Si{sub 3}N{sub 4} ceramics

Dai Jinhui,Li Jianbao,Chen Yongjun,Yang Liu,Sun Geliang
IF: 5.6
2003-01-01
Materials Research Bulletin
Abstract:The {beta}-Si{sub 3}N{sub 4} particles were prepared by heating original {alpha}-Si{sub 3}N{sub 4} powder with rare earth oxide Nd{sub 2}O{sub 3} or Yb{sub 2}O{sub 3} additives at 1600-1700 deg. C for 1.5 h. The transformation ratio of {alpha}-Si{sub 3}N{sub 4} was also investigated by XRD. The results showed that Yb{sub 2}O{sub 3} could accelerate the transformation of Si{sub 3}N{sub 4} more effectively than Nd{sub 2}O{sub 3} and the powder heated at 1700 deg. C with over 4 wt.% Yb{sub 2}O{sub 3} has a high transformation ratio of over 98%. The morphologies of the heated powders were observed by scanning electron microscopy. The results showed that the powder heated at 1700 deg. C with 4 wt.% Yb{sub 2}O{sub 3} had ideal {beta}-Si{sub 3}N{sub 4} rod-like morphology particles. This heated powder was used as a seed by adding it to the original {alpha}-Si{sub 3}N{sub 4} powder to prepare self-reinforced Si{sub 3}N{sub 4} ceramic by hot-pressed sintering. The fracture toughness of the seeded Si{sub 3}N{sub 4} ceramics increased to 9.1 MPa m{sup 1/2} from 7.6 MPa m{sup 1/2} of the unseeded Si{sub 3}N{sub 4} ceramics, while the high value of strength was still kept at 1200 deg. C.
What problem does this paper attempt to address?