Abstract:beta-Si3N4 with completeness of phase transformation and pole-liked morphology was developed by means of heating the initial Si3N4 powder with certain additive of Lu2O3. The influence of Lu2O3 on phase transformation and seeds morphology was investigated. The result showed that the beta-Si3N4 seeds with up to 95% beta phase content could be gotten with 1 mol% Lu2O3 as additive contents at 1750 degrees C for 2 h. The microstructure and mechanical properties of hot-pressed Si3N4 ceramics, using 10 mol% of Lu2O3 additives were investigated by means of MTS measurements and Vickers indentation crack size measurements, as well as XRD and SEM. It was known that the high fracture toughness of Si3N4 ceramics was attributed to the rodlike morphology of beta-Si3N4 grains. And the reinforcement effect and mechanism of beta-Si3N4 seed were studied. It was found that the grain size and its distribution influence on the property and microstructure of Si3N4 ceramics were investigated. The improvement in the fracture toughness with the amount of additive was mainly attributed to elongated grain growth during the sintering process. By this method, self-reinforced Si3N4 ceramics with an increment of 10 similar to 20% of fracture toughness was fabricated.

Preparation of β-Si3N4 Seeds and Self-reinforced Si3N4 Ceramics

Preparation of the Rod-Like Β-Si3n4 Particles Favoring the Self-Reinforcing Si3N4 Ceramics

Effect of the Residual Phases in Β-Si3n4 Seed on the Mechanical Properties of Self-Reinforced Si3N4 Ceramics

Preparation of the rod-like {beta}-Si{sub 3}N{sub 4} particles favoring the self-reinforcing Si{sub 3}N{sub 4} ceramics

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

Preparation and Characterization of Rod-Like Β-Si<sub>3</sub>n<sub>4</sub> Seeds

New Route to Improve the Fracture Toughness and Flexural Strength of Si3N4 Ceramics by Adding FeSi2

Preparation of β-Si3N4 Single Crystal Particles

Study on the Preparation,Properties and Mechnism of β-Si_3N_4 Crystal Seeds

Fabrication and Characterization of β-Si3N4 Seeds with Additive of Lu2O3

Microstructure characterization of hot-pressed β-silicon nitride containing β-Si3N4 seeds

Effects of Β-Si3n4 Seeds Addition on Microstructure and Mechanical Properties of Porous Si3N4 Ceramics

Effect of Seed Crystal Properties on the Microstructure of Si<sub>3</sub>N<sub>4</sub> Ceramics

Mechanical Property and Oxidation Behavior of Self-Reinforced Si3N4 Doped with Re2O3 (Re=Yb, Lu)

Microstructure and Properties of Si3N4 Ceramics Obtained from Addition of Β-Phase Seeds and Celsian

Microstructure and Performance of Silicon Nitride Ceramics with Lu2O3 Additives

Effects of seeds on the thermal conductivity of self-toughened Si3N4 ceramics

Effects of α-Si3N4 seeds and sintering additives on properties of porous silicon nitride ceramics fabricated by carbothermal reduction

Preparation of graded silicon nitride ceramics with high mechanical performance using β-Si 3 N 4 seeds

Synthesis of Fibrous Β-Si3n4 Structured Porous Ceramics Using Carbothermal Nitridation of Silica